Steel Super Invar-ANN vs Super Invar CR-H
Steel · Super Invar temper comparison
Super Invar-ANN and Super Invar CR-H are two conditions of the same steel grade, Super Invar: ANN (annealed) versus CR-H (cold Rolled Hard). The chemistry is identical, so every difference below comes from the condition. Super Invar CR-H is the stronger of the two: yield strength 650 MPa (94.3 ksi) against 300 MPa (43.5 ksi) for Super Invar-ANN, about 117% more; tensile strength follows at 750 MPa (109 ksi) vs 500 MPa (72.5 ksi). In exchange, Super Invar-ANN is the more ductile: elongation 35% versus 5% for Super Invar CR-H, and Super Invar CR-H is harder (240 HB vs 150 HB). Super Invar CR-H runs hotter in service (200°C vs 150°C continuous). On the shop floor, Super Invar-ANN welds better (very good vs good).
Super Invar-ANNChoose it when the part is bent, formed or impact-loaded, or when it will be welded.
Super Invar CR-HChoose it when strength drives the design, or when the part sees heat.
Super Invar-ANN vs Super Invar CR-H: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Super Invar-ANNSuper Invar CR-H
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Shear Modulus 57 GPa8.3 Msi · Bulk Modulus 110 GPa16 Msi · Poisson's Ratio 0.28 · Fracture Toughness (K_IC) 100 MPa·√m91 ksi·√in
Physical
Density and transition temperatures.
Same in both: Density 8.15 g/cm³0.29 lb/in³ · Melting Point (Solidus) 1,425°C2,597 °F · Liquidus Temperature 1,450°C2,642 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 10.5 W/m·K6.1 BTU/hr·ft·°F · Specific Heat Capacity 515 J/kg·K0.12 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 0.5 µm/m·K0.28 µin/in·°F · Min Service Temperature -50°C-58 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.6 V · Corrosion Resistance 28 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 70 / 100 · Polishability 65 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 75 MJ/kg32,244 BTU/lb · Embodied Carbon (primary production) 5.5 kg CO₂/kg · Embodied Water 130 L/kg15.6 gal/lb · Typical Recycled Content 25%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Super Invar-ANN vs Super Invar CR-H — frequently asked
Is Super Invar CR-H stronger than Super Invar-ANN?
Yes. Super Invar CR-H has a typical yield strength of 650 MPa (94.3 ksi) against 300 MPa (43.5 ksi) for Super Invar-ANN — about 117% more. Tensile strength is 750 MPa (109 ksi) vs 500 MPa (72.5 ksi).
Which condition does FabDigit quote by default, ANN or CR-H?
ANN is the default Super Invar condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which welds better, Super Invar-ANN or Super Invar CR-H?
Super Invar-ANN. Its weldability rates very good (70/100) against good (60/100) for Super Invar CR-H.
Ready to make it?
Upload a CAD file and FabDigit prices the part in Super Invar-ANN and Super Invar CR-H side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.