Steel SUP11A-A vs SUP11A-HR
Steel · SUP11A temper comparison
SUP11A-A and SUP11A-HR are two conditions of the same steel grade, SUP11A: A (solution annealed) versus HR (hot rolled). The chemistry is identical, so every difference below comes from the condition. SUP11A-HR is the stronger of the two: yield strength 550 MPa (79.8 ksi) against 420 MPa (60.9 ksi) for SUP11A-A, about 31% more; tensile strength follows at 900 MPa (131 ksi) vs 700 MPa (102 ksi). In exchange, SUP11A-A is the more ductile: elongation 22% versus 14% for SUP11A-HR, and SUP11A-HR is harder (270 HB vs 210 HB). SUP11A-HR runs hotter in service (300°C vs 230°C continuous). On the shop floor, SUP11A-A machines more easily (50 vs 35 out of 100).
SUP11A-AChoose it when the part is bent, formed or impact-loaded, or when the part is machined in volume.
SUP11A-HRChoose it when strength drives the design, or when the part sees heat.
SUP11A-A vs SUP11A-HR: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell C
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 206 GPa29.9 Msi · Shear Modulus 79 GPa11.5 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,420°C2,588 °F · Liquidus Temperature 1,480°C2,696 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 44 W/m·K25.4 BTU/hr·ft·°F · Specific Heat Capacity 470 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 12.3 µm/m·K6.8 µin/in·°F · Latent Heat of Fusion 250 J/g107 BTU/lb · Min Service Temperature -40°C-40 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.6 V · Corrosion Resistance 10 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 25 / 100 · Polishability 55 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 27 MJ/kg11,608 BTU/lb · Embodied Carbon (primary production) 2.1 kg CO₂/kg · Embodied Water 60 L/kg7.2 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
SUP11A-A vs SUP11A-HR — frequently asked
Is SUP11A-HR stronger than SUP11A-A?
Yes. SUP11A-HR has a typical yield strength of 550 MPa (79.8 ksi) against 420 MPa (60.9 ksi) for SUP11A-A — about 31% more. Tensile strength is 900 MPa (131 ksi) vs 700 MPa (102 ksi).
Which condition does FabDigit quote by default, A or HR?
QT-SPRING is the default SUP11A condition in the FabDigit quote flow (neither A nor HR). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, SUP11A-A or SUP11A-HR?
SUP11A-A, by a small margin. Both rate fair for machinability — 50/100 against 35/100 for SUP11A-HR; for welding the order is SUP11A-HR first (poor, 30/100) then SUP11A-A (poor, 25/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in SUP11A-A and SUP11A-HR side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.