Steel SPA-H CR-A vs SPA-H-HR
Steel · SPA-H temper comparison
SPA-H CR-A and SPA-H-HR are two conditions of the same steel grade, SPA-H: CR-A (cold rolled and annealed thin sheet) versus HR (hot rolled). The chemistry is identical, so every difference below comes from the condition. SPA-H-HR is the stronger of the two: yield strength 390 MPa (56.6 ksi) against 370 MPa (53.7 ksi) for SPA-H CR-A, about 5% more. In exchange, SPA-H CR-A is the more ductile: elongation 32% versus 28% for SPA-H-HR, and SPA-H-HR is harder (160 HB vs 150 HB).
SPA-H CR-AChoose it when the part is bent, formed or impact-loaded.
SPA-H-HRChoose it when strength drives the design.
SPA-H CR-A vs SPA-H-HR: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 205 GPa29.7 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29 · Fracture Toughness (K_IC) 100 MPa·√m91 ksi·√in
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,480°C2,696 °F · Liquidus Temperature 1,520°C2,768 °F
Thermal
How each material carries heat and how hot it can run.
Same in both: Thermal Conductivity 50 W/m·K28.9 BTU/hr·ft·°F · Specific Heat Capacity 470 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 12.2 µm/m·K6.8 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Max Service Temperature (continuous) 350°C662 °F · Min Service Temperature -20°C-4 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 7.8 % IACS · Electrical Resistivity 2.2×10⁻⁷ Ω·m8.66 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.62 V · Corrosion Resistance 32 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Same in both: Weldability 80 / 100 · Brazeability / Solderability 60 / 100 · Polishability 45 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 25 MJ/kg10,748 BTU/lb · Embodied Carbon (primary production) 2.1 kg CO₂/kg · Embodied Water 45 L/kg5.4 gal/lb · Typical Recycled Content 25%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
SPA-H CR-A vs SPA-H-HR — frequently asked
Is SPA-H-HR stronger than SPA-H CR-A?
Yes. SPA-H-HR has a typical yield strength of 390 MPa (56.6 ksi) against 370 MPa (53.7 ksi) for SPA-H CR-A — about 5% more. Tensile strength is 520 MPa (75.4 ksi) vs 500 MPa (72.5 ksi).
Which condition does FabDigit quote by default, CR-A or HR?
HR is the default SPA-H condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose SPA-H CR-A over SPA-H-HR?
Pick SPA-H CR-A when the part is bent, formed or impact-loaded. Pick SPA-H-HR when strength drives the design.
Ready to make it?
Upload a CAD file and FabDigit prices the part in SPA-H CR-A and SPA-H-HR side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.