Steel SKH51 Annealed vs SKH51 QT 62-64 HRC
Steel · SKH51 temper comparison
SKH51 Annealed and SKH51 QT 62-64 HRC are two conditions of the same steel grade, SKH51: Annealed versus QT 62-64 HRC (hardened & triple tempered to 62–64 HRC). The chemistry is identical, so every difference below comes from the condition. SKH51 QT 62-64 HRC is the stronger of the two: tensile strength 2,500 MPa (363 ksi) against 850 MPa (123 ksi) for SKH51 Annealed, about 194% more. In exchange, SKH51 Annealed is the more ductile: elongation 20% versus 0.3% for SKH51 QT 62-64 HRC, and SKH51 QT 62-64 HRC is harder (63 HRC vs 22 HRC). SKH51 QT 62-64 HRC is stiffer (230 GPa vs 217 GPa) and SKH51 QT 62-64 HRC runs hotter in service (560°C vs 400°C continuous). On the shop floor, SKH51 Annealed machines more easily (poor vs not recommended).
SKH51 AnnealedChoose it when the part is bent, formed or impact-loaded, or when the part is machined in volume.
SKH51 QT 62-64 HRCChoose it when strength drives the design, or when the part sees heat.
SKH51 Annealed vs SKH51 QT 62-64 HRC: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
SKH51 AnnealedSKH51 QT 62-64 HRC
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Elongation at Break
Compressive Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Rockwell C
Hardness, Vickers
Same in both: Shear Modulus 84 GPa12.2 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.28 · Yield Strength (0.2% offset) 550 MPa79.8 ksi · Reduction in Area 35% · Shear Strength 560 MPa81.2 ksi · Hardness, Brinell 240 HB · Hardness, Rockwell B 99 HRB
Physical
Density and transition temperatures.
Same in both: Density 8.16 g/cm³0.29 lb/in³ · Melting Point (Solidus) 1,370°C2,498 °F · Liquidus Temperature 1,450°C2,642 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 22 W/m·K12.7 BTU/hr·ft·°F · Specific Heat Capacity 420 J/kg·K0.1 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 11 µm/m·K6.1 µin/in·°F · Latent Heat of Fusion 250 J/g107 BTU/lb · Min Service Temperature -60°C-76 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 2.9 % IACS · Electrical Resistivity 5.9×10⁻⁷ Ω·m23.2 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Corrosion Resistance 16 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Same in both: Machinability Rating (AISI 1212 = 100 %) 35% · Weldability 20 / 100 · Formability (cold) 15 / 100 · Castability 25 / 100 · Brazeability / Solderability 55 / 100 · Polishability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 45 MJ/kg19,347 BTU/lb · Embodied Carbon (primary production) 3.2 kg CO₂/kg · Embodied Water 70 L/kg8.4 gal/lb · Typical Recycled Content 45%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
SKH51 Annealed vs SKH51 QT 62-64 HRC — frequently asked
Is SKH51 QT 62-64 HRC stronger than SKH51 Annealed?
Yes. SKH51 QT 62-64 HRC has a typical tensile strength of 2,500 MPa (363 ksi) against 850 MPa (123 ksi) for SKH51 Annealed — about 194% more.
Which condition does FabDigit quote by default, Annealed or QT 62-64 HRC?
Annealed is the default SKH51 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, SKH51 Annealed or SKH51 QT 62-64 HRC?
SKH51 Annealed. Its machinability rates poor (30/100) against not recommended (4/100) for SKH51 QT 62-64 HRC.