Steel S235J2W +AR vs S235J2W-CR
Steel · S235J2W temper comparison
S235J2W +AR and S235J2W-CR are two conditions of the same steel grade, S235J2W: +AR (hot rolled) versus CR (cold rolled). The chemistry is identical, so every difference below comes from the condition. S235J2W-CR is the stronger of the two: yield strength 380 MPa (55.1 ksi) against 265 MPa (38.4 ksi) for S235J2W +AR, about 43% more; tensile strength follows at 480 MPa (69.6 ksi) vs 420 MPa (60.9 ksi). In exchange, S235J2W +AR is the more ductile: elongation 30% versus 18% for S235J2W-CR, and S235J2W-CR is harder (150 HB vs 125 HB). S235J2W +AR runs hotter in service (350°C vs 300°C continuous).
S235J2W +ARChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
S235J2W-CRChoose it when strength drives the design.
S235J2W +AR vs S235J2W-CR: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 210 GPa30.5 Msi · Shear Modulus 81 GPa11.7 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.3
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,470°C2,678 °F · Liquidus Temperature 1,520°C2,768 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 48 W/m·K27.7 BTU/hr·ft·°F · Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 12 µm/m·K6.7 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Min Service Temperature -20°C-4 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 8.6 % IACS · Electrical Resistivity 2×10⁻⁷ Ω·m7.87 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.6 V · Corrosion Resistance 30 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 60 / 100 · Polishability 45 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 25 MJ/kg10,748 BTU/lb · Embodied Carbon (primary production) 1.9 kg CO₂/kg · Embodied Water 45 L/kg5.4 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
S235J2W +AR vs S235J2W-CR — frequently asked
Is S235J2W-CR stronger than S235J2W +AR?
Yes. S235J2W-CR has a typical yield strength of 380 MPa (55.1 ksi) against 265 MPa (38.4 ksi) for S235J2W +AR — about 43% more. Tensile strength is 480 MPa (69.6 ksi) vs 420 MPa (60.9 ksi).
Which condition does FabDigit quote by default, +AR or CR?
+AR is the default S235J2W condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose S235J2W +AR over S235J2W-CR?
Pick S235J2W +AR when the part is bent, formed or impact-loaded, or when the part sees heat. Pick S235J2W-CR when strength drives the design.
Ready to make it?
Upload a CAD file and FabDigit prices the part in S235J2W +AR and S235J2W-CR side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.