Steel Q345B-CR vs Q345B-HR
Steel · Q345B temper comparison
Q345B-CR and Q345B-HR are two conditions of the same steel grade, Q345B: CR (cold rolled) versus HR (hot rolled). The chemistry is identical, so every difference below comes from the condition. Q345B-CR is the stronger of the two: yield strength 450 MPa (65.3 ksi) against 365 MPa (52.9 ksi) for Q345B-HR, about 23% more; tensile strength follows at 560 MPa (81.2 ksi) vs 510 MPa (74 ksi). In exchange, Q345B-HR is the more ductile: elongation 24% versus 16% for Q345B-CR, and Q345B-CR is harder (180 HB vs 160 HB).
Q345B-CRChoose it when strength drives the design.
Q345B-HRChoose it when the part is bent, formed or impact-loaded.
Q345B-CR vs Q345B-HR: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Same in both: Elastic (Young's) Modulus 206 GPa29.9 Msi · Shear Modulus 79 GPa11.5 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.3 · Reduction in Area 50% · Compressive Strength 365 MPa52.9 ksi · Shear Strength 340 MPa49.3 ksi · Fracture Toughness (K_IC) 120 MPa·√m109 ksi·√in · Hardness, Vickers 168 HV
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,460°C2,660 °F · Liquidus Temperature 1,510°C2,750 °F
Thermal
How each material carries heat and how hot it can run.
Same in both: Thermal Conductivity 47 W/m·K27.2 BTU/hr·ft·°F · Specific Heat Capacity 470 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 12 µm/m·K6.7 µin/in·°F · Latent Heat of Fusion 247 J/g106 BTU/lb · Max Service Temperature (continuous) 400°C752 °F · Min Service Temperature -20°C-4 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 8.6 % IACS · Electrical Resistivity 2×10⁻⁷ Ω·m7.87 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.62 V · Corrosion Resistance 12 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Formability (cold)
Polishability
Same in both: Machinability Rating (AISI 1212 = 100 %) 58% · Weldability 85 / 100 · Brazeability / Solderability 55 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 25 MJ/kg10,748 BTU/lb · Embodied Carbon (primary production) 2.1 kg CO₂/kg · Embodied Water 40 L/kg4.8 gal/lb · Typical Recycled Content 25%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Q345B-CR vs Q345B-HR — frequently asked
Is Q345B-CR stronger than Q345B-HR?
Yes. Q345B-CR has a typical yield strength of 450 MPa (65.3 ksi) against 365 MPa (52.9 ksi) for Q345B-HR — about 23% more. Tensile strength is 560 MPa (81.2 ksi) vs 510 MPa (74 ksi).
Which condition does FabDigit quote by default, CR or HR?
HR is the default Q345B condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose Q345B-CR over Q345B-HR?
Pick Q345B-CR when strength drives the design. Pick Q345B-HR when the part is bent, formed or impact-loaded.
Ready to make it?
Upload a CAD file and FabDigit prices the part in Q345B-CR and Q345B-HR side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.