Steel NAK55 Nitrided vs NAK55 Q&T
Steel · NAK55 temper comparison
NAK55 Nitrided and NAK55 Q&T are two conditions of the same steel grade, NAK55: Nitrided versus Q&T (quenched and tempered). The chemistry is identical, so every difference below comes from the condition. Both yield at about 1,100 MPa — the mechanical properties are the same, and the difference is in how the stock is processed and what it is certified to (Nitrided versus quenched and tempered). NAK55 Q&T is the more ductile: elongation 9% versus 8% for NAK55 Nitrided, and NAK55 Nitrided is harder (680 HV vs 404 HV). On the shop floor, NAK55 Q&T machines more easily (fair vs poor) and NAK55 Q&T welds better (fair vs not recommended).
NAK55 Q&TChoose it when the part is bent, formed or impact-loaded, or when the part is machined in volume.
NAK55 Nitrided vs NAK55 Q&T: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell C
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 206 GPa29.9 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 165 GPa23.9 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Same in both: Density 7.8 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,420°C2,588 °F · Liquidus Temperature 1,480°C2,696 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 12.4 µm/m·K6.9 µin/in·°F · Min Service Temperature -20°C-4 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Resistivity 2.6×10⁻⁷ Ω·m10.2 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Polishability
Same in both: Brazeability / Solderability 30 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 34 MJ/kg14,617 BTU/lb · Embodied Carbon (primary production) 2.5 kg CO₂/kg · Embodied Water 55 L/kg6.6 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
NAK55 Nitrided vs NAK55 Q&T — frequently asked
What is the difference between NAK55 Nitrided and NAK55 Q&T?
NAK55 Nitrided and NAK55 Q&T are two conditions of the same steel grade, NAK55: Nitrided versus Q&T (quenched and tempered). The chemistry is identical, so every difference below comes from the condition. Both yield at about 1,100 MPa — the mechanical properties are the same, and the difference is in how the stock is processed and what it is certified to (Nitrided versus quenched and tempered).
Which condition does FabDigit quote by default, Nitrided or Q&T?
Annealed is the default NAK55 condition in the FabDigit quote flow (neither Nitrided nor Q&T). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, NAK55 Nitrided or NAK55 Q&T?
NAK55 Q&T. Its machinability rates fair (52/100) against poor (15/100) for NAK55 Nitrided; for welding the order is NAK55 Q&T first (fair, 40/100) then NAK55 Nitrided (not recommended, 8/100).