Steel H13 Annealed vs H13 Q&T
Steel · H13 temper comparison
H13 Annealed and H13 Q&T are two conditions of the same steel grade, H13: Annealed versus Q&T (quenched and tempered). The chemistry is identical, so every difference below comes from the condition. H13 Q&T is the stronger of the two: yield strength 1,400 MPa (203 ksi) against 520 MPa (75.4 ksi) for H13 Annealed, about 169% more; tensile strength follows at 1,620 MPa (235 ksi) vs 760 MPa (110 ksi). In exchange, H13 Annealed is the more ductile: elongation 25% versus 12% for H13 Q&T, and H13 Q&T is harder (480 HV vs 215 HV). H13 Q&T runs hotter in service (540°C vs 400°C continuous). On the shop floor, H13 Annealed machines more easily (fair vs poor).
H13 AnnealedChoose it when the part is bent, formed or impact-loaded, or when the part is machined in volume.
H13 Q&TChoose it when strength drives the design, or when the part sees heat.
H13 Annealed vs H13 Q&T: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 210 GPa30.5 Msi · Shear Modulus 81 GPa11.7 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.3 · Hardness, Brinell 205 HB · Hardness, Rockwell B 95 HRB
Physical
Density and transition temperatures.
Same in both: Density 7.8 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,425°C2,597 °F · Liquidus Temperature 1,480°C2,696 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 24.5 W/m·K14.2 BTU/hr·ft·°F · Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 10.9 µm/m·K6.1 µin/in·°F · Latent Heat of Fusion 250 J/g107 BTU/lb · Min Service Temperature -30°C-22 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 3.3 % IACS · Electrical Resistivity 5.2×10⁻⁷ Ω·m20.5 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.58 V · Corrosion Resistance 22 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Polishability
Same in both: Weldability 35 / 100 · Formability (cold) 20 / 100 · Brazeability / Solderability 30 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 34 MJ/kg14,617 BTU/lb · Embodied Carbon (primary production) 2.6 kg CO₂/kg · Embodied Water 75 L/kg9 gal/lb · Typical Recycled Content 45%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
H13 Annealed vs H13 Q&T — frequently asked
Is H13 Q&T stronger than H13 Annealed?
Yes. H13 Q&T has a typical yield strength of 1,400 MPa (203 ksi) against 520 MPa (75.4 ksi) for H13 Annealed — about 169% more. Tensile strength is 1,620 MPa (235 ksi) vs 760 MPa (110 ksi).
Which condition does FabDigit quote by default, Annealed or Q&T?
Annealed is the default H13 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, H13 Annealed or H13 Q&T?
H13 Annealed. Its machinability rates fair (45/100) against poor (15/100) for H13 Q&T.
Ready to make it?
Upload a CAD file and FabDigit prices the part in H13 Annealed and H13 Q&T side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.