Steel GCr9-N vs GCr9 QT60-64HRC
Steel · GCr9 temper comparison
GCr9-N and GCr9 QT60-64HRC are two conditions of the same steel grade, GCr9: N (normalized) versus QT60-64HRC (quenched & low-temperature tempered, 60–64 HRC). The chemistry is identical, so every difference below comes from the condition. GCr9 QT60-64HRC is the stronger of the two: yield strength 1,750 MPa (254 ksi) against 600 MPa (87 ksi) for GCr9-N, about 192% more; tensile strength follows at 2,150 MPa (312 ksi) vs 1,000 MPa (145 ksi). In exchange, GCr9-N is the more ductile: elongation 10% versus 1% for GCr9 QT60-64HRC, and GCr9-N is harder (300 HB vs 190 HB). GCr9-N runs hotter in service (200°C vs 150°C continuous) and GCr9-N conducts heat better (43 W/m·K vs 38 W/m·K). On the shop floor, GCr9-N machines more easily (poor vs not recommended).
GCr9-NChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
GCr9 QT60-64HRCChoose it when strength drives the design.
GCr9-N vs GCr9 QT60-64HRC: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.3
Physical
Density and transition temperatures.
Same in both: Density 7.81 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,425°C2,597 °F · Liquidus Temperature 1,470°C2,678 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 12 µm/m·K6.7 µin/in·°F · Latent Heat of Fusion 250 J/g107 BTU/lb · Min Service Temperature -60°C-76 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 7 % IACS · Electrical Resistivity 2.5×10⁻⁷ Ω·m9.84 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.6 V · Corrosion Resistance 12 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Polishability
Same in both: Brazeability / Solderability 35 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 30 MJ/kg12,898 BTU/lb · Embodied Carbon (primary production) 2.2 kg CO₂/kg · Embodied Water 55 L/kg6.6 gal/lb · Typical Recycled Content 25%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
GCr9-N vs GCr9 QT60-64HRC — frequently asked
Is GCr9 QT60-64HRC stronger than GCr9-N?
Yes. GCr9 QT60-64HRC has a typical yield strength of 1,750 MPa (254 ksi) against 600 MPa (87 ksi) for GCr9-N — about 192% more. Tensile strength is 2,150 MPa (312 ksi) vs 1,000 MPa (145 ksi).
Which condition does FabDigit quote by default, N or QT60-64HRC?
A is the default GCr9 condition in the FabDigit quote flow (neither N nor QT60-64HRC). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, GCr9-N or GCr9 QT60-64HRC?
GCr9-N. Its machinability rates poor (25/100) against not recommended (10/100) for GCr9 QT60-64HRC; for welding the order is GCr9 QT60-64HRC first (poor, 15/100) then GCr9-N (not recommended, 10/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in GCr9-N and GCr9 QT60-64HRC side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.