Steel G15CrMoV6-9 +A vs G15CrMoV6-9 +QT2
Steel · G15CrMoV6-9 temper comparison
G15CrMoV6-9 +A and G15CrMoV6-9 +QT2 are two conditions of the same steel grade, G15CrMoV6-9: +A (annealed) versus +QT2 (quenched and tempered, higher strength class). The chemistry is identical, so every difference below comes from the condition. G15CrMoV6-9 +QT2 is the stronger of the two: yield strength 580 MPa (84.1 ksi) against 340 MPa (49.3 ksi) for G15CrMoV6-9 +A, about 71% more; tensile strength follows at 760 MPa (110 ksi) vs 560 MPa (81.2 ksi). In exchange, G15CrMoV6-9 +A is the more ductile: elongation 22% versus 14% for G15CrMoV6-9 +QT2, and G15CrMoV6-9 +QT2 is harder (240 HB vs 165 HB). G15CrMoV6-9 +QT2 runs hotter in service (540°C vs 450°C continuous). On the shop floor, G15CrMoV6-9 +A machines more easily (good vs fair) and G15CrMoV6-9 +A welds better (good vs fair).
G15CrMoV6-9 +AChoose it when the part is bent, formed or impact-loaded, or when the part is machined in volume.
G15CrMoV6-9 +QT2Choose it when strength drives the design, or when the part sees heat.
G15CrMoV6-9 +A vs G15CrMoV6-9 +QT2: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
G15CrMoV6-9 +AG15CrMoV6-9 +QT2
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell C
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 210 GPa30.5 Msi · Shear Modulus 81 GPa11.7 Msi · Bulk Modulus 165 GPa23.9 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,425°C2,597 °F · Liquidus Temperature 1,505°C2,741 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 12.3 µm/m·K6.8 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Min Service Temperature -20°C-4 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.6 V · Corrosion Resistance 15 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 60 / 100 · Brazeability / Solderability 45 / 100 · Polishability 50 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 24 MJ/kg10,318 BTU/lb · Embodied Carbon (primary production) 2 kg CO₂/kg · Embodied Water 50 L/kg6 gal/lb · Typical Recycled Content 60%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
G15CrMoV6-9 +A vs G15CrMoV6-9 +QT2 — frequently asked
Is G15CrMoV6-9 +QT2 stronger than G15CrMoV6-9 +A?
Yes. G15CrMoV6-9 +QT2 has a typical yield strength of 580 MPa (84.1 ksi) against 340 MPa (49.3 ksi) for G15CrMoV6-9 +A — about 71% more. Tensile strength is 760 MPa (110 ksi) vs 560 MPa (81.2 ksi).
Which condition does FabDigit quote by default, +A or +QT2?
+QT1 is the default G15CrMoV6-9 condition in the FabDigit quote flow (neither +A nor +QT2). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, G15CrMoV6-9 +A or G15CrMoV6-9 +QT2?
G15CrMoV6-9 +A. Its machinability rates good (55/100) against fair (38/100) for G15CrMoV6-9 +QT2; for welding the order is G15CrMoV6-9 +A first (good, 58/100) then G15CrMoV6-9 +QT2 (fair, 45/100).