Steel E90C-B9-AW vs E90C-B9 N+T
Steel · E90C-B9 temper comparison
E90C-B9-AW and E90C-B9 N+T are two conditions of the same steel grade, E90C-B9: AW (as-welded deposit) versus N+T (normalized and tempered). The chemistry is identical, so every difference below comes from the condition. E90C-B9-AW is the stronger of the two: yield strength 900 MPa (131 ksi) against 580 MPa (84.1 ksi) for E90C-B9 N+T, about 55% more; tensile strength follows at 1,150 MPa (167 ksi) vs 700 MPa (102 ksi). In exchange, E90C-B9 N+T is the more ductile: elongation 22% versus 9% for E90C-B9-AW, and E90C-B9-AW is harder (400 HB vs 235 HB). E90C-B9 N+T runs hotter in service (620°C vs 0°C continuous). On the shop floor, E90C-B9 N+T machines more easily (fair vs not recommended).
E90C-B9-AWChoose it when strength drives the design.
E90C-B9 N+TChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
E90C-B9-AW vs E90C-B9 N+T: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell C
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 218 GPa31.6 Msi · Shear Modulus 84 GPa12.2 Msi · Bulk Modulus 165 GPa23.9 Msi · Poisson's Ratio 0.3
Physical
Density and transition temperatures.
Same in both: Density 7.75 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,425°C2,597 °F · Liquidus Temperature 1,500°C2,732 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 26 W/m·K15 BTU/hr·ft·°F · Specific Heat Capacity 480 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 10.8 µm/m·K6 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Min Service Temperature -20°C-4 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Resistivity 6×10⁻⁷ Ω·m23.6 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.45 V · Corrosion Resistance 30 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Same in both: Weldability 45 / 100 · Polishability 55 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 38 MJ/kg16,337 BTU/lb · Embodied Carbon (primary production) 2.9 kg CO₂/kg · Embodied Water 70 L/kg8.4 gal/lb · Typical Recycled Content 25%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
E90C-B9-AW vs E90C-B9 N+T — frequently asked
Is E90C-B9-AW stronger than E90C-B9 N+T?
Yes. E90C-B9-AW has a typical yield strength of 900 MPa (131 ksi) against 580 MPa (84.1 ksi) for E90C-B9 N+T — about 55% more. Tensile strength is 1,150 MPa (167 ksi) vs 700 MPa (102 ksi).
Which condition does FabDigit quote by default, AW or N+T?
PWHT760 is the default E90C-B9 condition in the FabDigit quote flow (neither AW nor N+T). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, E90C-B9-AW or E90C-B9 N+T?
E90C-B9 N+T. Its machinability rates fair (40/100) against not recommended (12/100) for E90C-B9-AW.