Steel E370 +C vs E370-IH
Steel · E370 temper comparison
E370 +C and E370-IH are two conditions of the same steel grade, E370: +C (cold drawn) versus IH (induction hardened). The chemistry is identical, so every difference below comes from the condition. E370 +C is the stronger of the two: yield strength 620 MPa (89.9 ksi) against 400 MPa (58 ksi) for E370-IH, about 55% more; tensile strength follows at 800 MPa (116 ksi) vs 720 MPa (104 ksi). In exchange, E370-IH is the more ductile: elongation 8% versus 7% for E370 +C, and E370-IH is harder (560 HB vs 235 HB). E370 +C runs hotter in service (350°C vs 200°C continuous). On the shop floor, E370 +C machines more easily (good vs not recommended) and E370 +C welds better (30 vs 15 out of 100).
E370 +CChoose it when strength drives the design, or when the part sees heat.
E370-IHChoose it when the part is bent, formed or impact-loaded.
E370 +C vs E370-IH: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 210 GPa30.5 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29 · Reduction in Area 25% · Hardness, Rockwell B 95 HRB
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,425°C2,597 °F · Liquidus Temperature 1,490°C2,714 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 470 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 11.8 µm/m·K6.6 µin/in·°F · Latent Heat of Fusion 250 J/g107 BTU/lb · Min Service Temperature -20°C-4 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.61 V · Corrosion Resistance 10 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 55 / 100 · Polishability 50 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 25 MJ/kg10,748 BTU/lb · Embodied Carbon (primary production) 2.1 kg CO₂/kg · Embodied Water 45 L/kg5.4 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
E370 +C vs E370-IH — frequently asked
Is E370 +C stronger than E370-IH?
Yes. E370 +C has a typical yield strength of 620 MPa (89.9 ksi) against 400 MPa (58 ksi) for E370-IH — about 55% more. Tensile strength is 800 MPa (116 ksi) vs 720 MPa (104 ksi).
Which condition does FabDigit quote by default, +C or IH?
+AR is the default E370 condition in the FabDigit quote flow (neither +C nor IH). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, E370 +C or E370-IH?
E370 +C. Its machinability rates good (58/100) against not recommended (12/100) for E370-IH; for welding the order is E370 +C first (poor, 30/100) then E370-IH (poor, 15/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in E370 +C and E370-IH side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.