Steel C45 +C vs C45 Normalized
Steel · C45 temper comparison
C45 +C and C45 Normalized are two conditions of the same steel grade, C45: +C (cold drawn) versus Normalized. The chemistry is identical, so every difference below comes from the condition. C45 +C is the stronger of the two: yield strength 580 MPa (84.1 ksi) against 400 MPa (58 ksi) for C45 Normalized, about 45% more; tensile strength follows at 700 MPa (102 ksi) vs 650 MPa (94.3 ksi). In exchange, C45 Normalized is the more ductile: elongation 17% versus 11% for C45 +C, and C45 +C is harder (210 HB vs 190 HB).
C45 +CChoose it when strength drives the design.
C45 NormalizedChoose it when the part is bent, formed or impact-loaded.
C45 +C vs C45 Normalized: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Same in both: Elastic (Young's) Modulus 210 GPa30.5 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29 · Compressive Strength 400 MPa58 ksi · Shear Strength 390 MPa56.6 ksi · Fracture Toughness (K_IC) 50 MPa·√m45.5 ksi·√in · Hardness, Vickers 200 HV
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,420°C2,588 °F · Liquidus Temperature 1,495°C2,723 °F
Thermal
How each material carries heat and how hot it can run.
Same in both: Thermal Conductivity 49 W/m·K28.3 BTU/hr·ft·°F · Specific Heat Capacity 486 J/kg·K0.12 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 11.7 µm/m·K6.5 µin/in·°F · Latent Heat of Fusion 247 J/g106 BTU/lb · Max Service Temperature (continuous) 400°C752 °F · Min Service Temperature -20°C-4 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 10 % IACS · Electrical Resistivity 1.7×10⁻⁷ Ω·m6.69 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.61 V · Corrosion Resistance 12 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Same in both: Weldability 45 / 100 · Castability 45 / 100 · Brazeability / Solderability 65 / 100 · Polishability 60 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 25 MJ/kg10,748 BTU/lb · Embodied Carbon (primary production) 2 kg CO₂/kg · Embodied Water 50 L/kg6 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
C45 +C vs C45 Normalized — frequently asked
Is C45 +C stronger than C45 Normalized?
Yes. C45 +C has a typical yield strength of 580 MPa (84.1 ksi) against 400 MPa (58 ksi) for C45 Normalized — about 45% more. Tensile strength is 700 MPa (102 ksi) vs 650 MPa (94.3 ksi).
Which condition does FabDigit quote by default, +C or Normalized?
Normalized is the default C45 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, C45 +C or C45 Normalized?
C45 +C, by a small margin. Both rate good for machinability — 62/100 against 55/100 for C45 Normalized.
Ready to make it?
Upload a CAD file and FabDigit prices the part in C45 +C and C45 Normalized side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.