Steel C20E2C-CH vs C20E2C +U
Steel · C20E2C temper comparison
C20E2C-CH and C20E2C +U are two conditions of the same steel grade, C20E2C: CH (carburized and hardened) versus +U (hot rolled). The chemistry is identical, so every difference below comes from the condition. C20E2C-CH is the stronger of the two: yield strength 420 MPa (60.9 ksi) against 250 MPa (36.3 ksi) for C20E2C +U, about 68% more; tensile strength follows at 620 MPa (89.9 ksi) vs 420 MPa (60.9 ksi). In exchange, C20E2C +U is the more ductile: elongation 28% versus 12% for C20E2C-CH, and C20E2C-CH is harder (180 HB vs 116 HB). C20E2C +U runs hotter in service (400°C vs 180°C continuous). On the shop floor, C20E2C +U machines more easily (good vs poor) and C20E2C +U welds better (excellent vs poor).
C20E2C-CHChoose it when strength drives the design.
C20E2C +UChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
C20E2C-CH vs C20E2C +U: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 207 GPa30 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29 · Compressive Strength 250 MPa36.3 ksi · Shear Strength 280 MPa40.6 ksi · Fracture Toughness (K_IC) 140 MPa·√m127 ksi·√in · Hardness, Rockwell B 66 HRB
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,425°C2,597 °F · Liquidus Temperature 1,515°C2,759 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 51.9 W/m·K30 BTU/hr·ft·°F · Specific Heat Capacity 475 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 11.7 µm/m·K6.5 µin/in·°F · Latent Heat of Fusion 247 J/g106 BTU/lb · Min Service Temperature -20°C-4 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 10.8 % IACS · Electrical Resistivity 1.6×10⁻⁷ Ω·m6.3 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.62 V · Corrosion Resistance 10 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 85 / 100 · Polishability 50 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 25 MJ/kg10,748 BTU/lb · Embodied Carbon (primary production) 1.9 kg CO₂/kg · Embodied Water 45 L/kg5.4 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
C20E2C-CH vs C20E2C +U — frequently asked
Is C20E2C-CH stronger than C20E2C +U?
Yes. C20E2C-CH has a typical yield strength of 420 MPa (60.9 ksi) against 250 MPa (36.3 ksi) for C20E2C +U — about 68% more. Tensile strength is 620 MPa (89.9 ksi) vs 420 MPa (60.9 ksi).
Which condition does FabDigit quote by default, CH or +U?
+U is the default C20E2C condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, C20E2C-CH or C20E2C +U?
C20E2C +U. Its machinability rates good (58/100) against poor (20/100) for C20E2C-CH; for welding the order is C20E2C +U first (excellent, 95/100) then C20E2C-CH (poor, 25/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in C20E2C-CH and C20E2C +U side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.