Steel C17C +C vs C17C Carburized
Steel · C17C temper comparison
C17C +C and C17C Carburized are two conditions of the same steel grade, C17C: +C (cold drawn) versus Carburized (carburized and hardened). The chemistry is identical, so every difference below comes from the condition. C17C Carburized is the stronger of the two: yield strength 480 MPa (69.6 ksi) against 450 MPa (65.3 ksi) for C17C +C, about 7% more; tensile strength follows at 700 MPa (102 ksi) vs 550 MPa (79.8 ksi). C17C Carburized is the more ductile: elongation 15% versus 12% for C17C +C, and C17C Carburized is harder (700 HV vs 168 HV). C17C +C runs hotter in service (300°C vs 180°C continuous). On the shop floor, C17C +C machines more easily (good vs poor) and C17C +C welds better (excellent vs poor).
C17C +CChoose it when the part sees heat, or when the part is machined in volume.
C17C CarburizedChoose it when strength drives the design, or when the part is bent, formed or impact-loaded.
C17C +C vs C17C Carburized: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 205 GPa29.7 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29 · Compressive Strength 450 MPa65.3 ksi · Shear Strength 340 MPa49.3 ksi · Hardness, Brinell 160 HB · Hardness, Rockwell B 83 HRB
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,495°C2,723 °F · Liquidus Temperature 1,520°C2,768 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 51 W/m·K29.5 BTU/hr·ft·°F · Specific Heat Capacity 470 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 11.9 µm/m·K6.6 µin/in·°F · Latent Heat of Fusion 247 J/g106 BTU/lb · Min Service Temperature -30°C-22 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 11 % IACS · Electrical Resistivity 1.59×10⁻⁷ Ω·m6.26 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.61 V · Corrosion Resistance 10 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Weldability
Formability (cold)
Same in both: Machinability Rating (AISI 1212 = 100 %) 70% · Brazeability / Solderability 75 / 100 · Polishability 50 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 25 MJ/kg10,748 BTU/lb · Embodied Carbon (primary production) 2 kg CO₂/kg · Embodied Water 40 L/kg4.8 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
C17C +C vs C17C Carburized — frequently asked
Is C17C Carburized stronger than C17C +C?
Yes. C17C Carburized has a typical yield strength of 480 MPa (69.6 ksi) against 450 MPa (65.3 ksi) for C17C +C — about 7% more. Tensile strength is 700 MPa (102 ksi) vs 550 MPa (79.8 ksi).
Which condition does FabDigit quote by default, +C or Carburized?
+C is the default C17C condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, C17C +C or C17C Carburized?
C17C +C. Its machinability rates good (55/100) against poor (15/100) for C17C Carburized; for welding the order is C17C +C first (excellent, 92/100) then C17C Carburized (poor, 25/100).