Steel C10E +A vs C10E +U
Steel · C10E temper comparison
C10E +A and C10E +U are two conditions of the same steel grade, C10E: +A (annealed) versus +U (hot rolled). The chemistry is identical, so every difference below comes from the condition. C10E +U is the stronger of the two: yield strength 235 MPa (34.1 ksi) against 210 MPa (30.5 ksi) for C10E +A, about 12% more; tensile strength follows at 400 MPa (58 ksi) vs 360 MPa (52.2 ksi). In exchange, C10E +A is the more ductile: elongation 36% versus 30% for C10E +U, and C10E +U is harder (115 HB vs 105 HB).
C10E +AChoose it when the part is bent, formed or impact-loaded.
C10E +UChoose it when strength drives the design.
C10E +A vs C10E +U: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 210 GPa30.5 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,495°C2,723 °F · Liquidus Temperature 1,520°C2,768 °F
Thermal
How each material carries heat and how hot it can run.
Same in both: Thermal Conductivity 50 W/m·K28.9 BTU/hr·ft·°F · Specific Heat Capacity 470 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 11.7 µm/m·K6.5 µin/in·°F · Latent Heat of Fusion 247 J/g106 BTU/lb · Max Service Temperature (continuous) 350°C662 °F · Min Service Temperature -30°C-22 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 10.8 % IACS · Electrical Resistivity 1.6×10⁻⁷ Ω·m6.3 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.61 V · Corrosion Resistance 10 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Same in both: Weldability 95 / 100 · Brazeability / Solderability 80 / 100 · Polishability 50 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 25 MJ/kg10,748 BTU/lb · Embodied Carbon (primary production) 2.1 kg CO₂/kg · Embodied Water 40 L/kg4.8 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
C10E +A vs C10E +U — frequently asked
Is C10E +U stronger than C10E +A?
Yes. C10E +U has a typical yield strength of 235 MPa (34.1 ksi) against 210 MPa (30.5 ksi) for C10E +A — about 12% more. Tensile strength is 400 MPa (58 ksi) vs 360 MPa (52.2 ksi).
Which condition does FabDigit quote by default, +A or +U?
+N is the default C10E condition in the FabDigit quote flow (neither +A nor +U). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose C10E +A over C10E +U?
Pick C10E +A when the part is bent, formed or impact-loaded. Pick C10E +U when strength drives the design.
Ready to make it?
Upload a CAD file and FabDigit prices the part in C10E +A and C10E +U side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.