Steel A842 Grade 300-ANN vs A842 Grade 300 AS-CAST
Steel · A842 Grade 300 temper comparison
A842 Grade 300-ANN and A842 Grade 300 AS-CAST are two conditions of the same steel grade, A842 Grade 300: ANN (annealed) versus AS-CAST. The chemistry is identical, so every difference below comes from the condition. A842 Grade 300 AS-CAST is the stronger of the two: yield strength 230 MPa (33.4 ksi) against 215 MPa (31.2 ksi) for A842 Grade 300-ANN, about 7% more; tensile strength follows at 330 MPa (47.9 ksi) vs 310 MPa (45 ksi). In exchange, A842 Grade 300-ANN is the more ductile: elongation 4% versus 2.5% for A842 Grade 300 AS-CAST, and A842 Grade 300 AS-CAST is harder (170 HB vs 150 HB). A842 Grade 300-ANN runs hotter in service (450°C vs 400°C continuous) and A842 Grade 300-ANN conducts heat better (42 W/m·K vs 36 W/m·K). On the shop floor, A842 Grade 300-ANN machines more easily (50 vs 40 out of 100).
A842 Grade 300-ANNChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
A842 Grade 300 AS-CASTChoose it when strength drives the design.
A842 Grade 300-ANN vs A842 Grade 300 AS-CAST: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
A842 Grade 300-ANNA842 Grade 300 AS-CAST
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Same in both: Shear Modulus 57 GPa8.3 Msi · Bulk Modulus 101 GPa14.6 Msi · Poisson's Ratio 0.26
Physical
Density and transition temperatures.
Same in both: Density 7.1 g/cm³0.26 lb/in³ · Melting Point (Solidus) 1,150°C2,102 °F · Liquidus Temperature 1,180°C2,156 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 470 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 11.5 µm/m·K6.4 µin/in·°F · Latent Heat of Fusion 220 J/g94.6 BTU/lb · Min Service Temperature -20°C-4 °F
Electrical
Conductivity and insulation.
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.6 V · Corrosion Resistance 16 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 65 / 100 · Brazeability / Solderability 40 / 100 · Polishability 35 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 19 MJ/kg8,169 BTU/lb · Embodied Carbon (primary production) 1.7 kg CO₂/kg · Embodied Water 40 L/kg4.8 gal/lb · Typical Recycled Content 90%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
A842 Grade 300-ANN vs A842 Grade 300 AS-CAST — frequently asked
Is A842 Grade 300 AS-CAST stronger than A842 Grade 300-ANN?
Yes. A842 Grade 300 AS-CAST has a typical yield strength of 230 MPa (33.4 ksi) against 215 MPa (31.2 ksi) for A842 Grade 300-ANN — about 7% more. Tensile strength is 330 MPa (47.9 ksi) vs 310 MPa (45 ksi).
Which condition does FabDigit quote by default, ANN or AS-CAST?
AS-CAST is the default A842 Grade 300 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, A842 Grade 300-ANN or A842 Grade 300 AS-CAST?
A842 Grade 300-ANN, by a small margin. Both rate fair for machinability — 50/100 against 40/100 for A842 Grade 300 AS-CAST; for welding the order is A842 Grade 300-ANN first (poor, 30/100) then A842 Grade 300 AS-CAST (poor, 25/100).