Steel A228-CD vs A228 CD-FINE
Steel · A228 temper comparison
A228-CD and A228 CD-FINE are two conditions of the same steel grade, A228: CD (cold drawn) versus CD-FINE. The chemistry is identical, so every difference below comes from the condition. A228 CD-FINE is the stronger of the two: yield strength 2,400 MPa (348 ksi) against 1,950 MPa (283 ksi) for A228-CD, about 23% more; tensile strength follows at 2,800 MPa (406 ksi) vs 2,300 MPa (334 ksi). In exchange, A228-CD is the more ductile: elongation 3% versus 2% for A228 CD-FINE, and A228 CD-FINE is harder (57 HRC vs 52 HRC). A228-CD runs hotter in service (120°C vs 100°C continuous).
A228-CDChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
A228 CD-FINEChoose it when strength drives the design.
A228-CD vs A228 CD-FINE: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Rockwell C
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 207 GPa30 Msi · Shear Modulus 79.3 GPa11.5 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29 · Hardness, Brinell 530 HB
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,400°C2,552 °F · Liquidus Temperature 1,470°C2,678 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 480 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 12.5 µm/m·K6.9 µin/in·°F · Latent Heat of Fusion 247 J/g106 BTU/lb · Min Service Temperature -50°C-58 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.65 V · Corrosion Resistance 10 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 45 / 100 · Polishability 60 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 27 MJ/kg11,608 BTU/lb · Embodied Carbon (primary production) 2.1 kg CO₂/kg · Embodied Water 60 L/kg7.2 gal/lb · Typical Recycled Content 25%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
A228-CD vs A228 CD-FINE — frequently asked
Is A228 CD-FINE stronger than A228-CD?
Yes. A228 CD-FINE has a typical yield strength of 2,400 MPa (348 ksi) against 1,950 MPa (283 ksi) for A228-CD — about 23% more. Tensile strength is 2,800 MPa (406 ksi) vs 2,300 MPa (334 ksi).
Which condition does FabDigit quote by default, CD or CD-FINE?
CD is the default A228 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose A228-CD over A228 CD-FINE?
Pick A228-CD when the part is bent, formed or impact-loaded, or when the part sees heat. Pick A228 CD-FINE when strength drives the design.
Ready to make it?
Upload a CAD file and FabDigit prices the part in A228-CD and A228 CD-FINE side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.