Steel 85-N vs 85 QT-50-55HRC
Steel · 85 temper comparison
85-N and 85 QT-50-55HRC are two conditions of the same steel grade, 85: N (normalized) versus QT-50-55HRC. The chemistry is identical, so every difference below comes from the condition. 85 QT-50-55HRC is the stronger of the two: yield strength 1,650 MPa (239 ksi) against 590 MPa (85.6 ksi) for 85-N, about 180% more; tensile strength follows at 1,850 MPa (268 ksi) vs 1,010 MPa (146 ksi). In exchange, 85-N is the more ductile: elongation 11% versus 3% for 85 QT-50-55HRC, and 85 QT-50-55HRC is harder (375 HB vs 300 HB). 85-N runs hotter in service (250°C vs 160°C continuous). On the shop floor, 85-N machines more easily (fair vs not recommended).
85-NChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
85 QT-50-55HRCChoose it when strength drives the design.
85-N vs 85 QT-50-55HRC: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell C
Hardness, Vickers
Same in both: Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Same in both: Density 7.81 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,400°C2,552 °F · Liquidus Temperature 1,480°C2,696 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 470 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 11.5 µm/m·K6.4 µin/in·°F · Latent Heat of Fusion 250 J/g107 BTU/lb · Min Service Temperature -40°C-40 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.6 V · Corrosion Resistance 10 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Same in both: Weldability 15 / 100 · Brazeability / Solderability 45 / 100 · Polishability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 30 MJ/kg12,898 BTU/lb · Embodied Carbon (primary production) 2.2 kg CO₂/kg · Embodied Water 45 L/kg5.4 gal/lb · Typical Recycled Content 25%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
85-N vs 85 QT-50-55HRC — frequently asked
Is 85 QT-50-55HRC stronger than 85-N?
Yes. 85 QT-50-55HRC has a typical yield strength of 1,650 MPa (239 ksi) against 590 MPa (85.6 ksi) for 85-N — about 180% more. Tensile strength is 1,850 MPa (268 ksi) vs 1,010 MPa (146 ksi).
Which condition does FabDigit quote by default, N or QT-50-55HRC?
QT is the default 85 condition in the FabDigit quote flow (neither N nor QT-50-55HRC). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 85-N or 85 QT-50-55HRC?
85-N. Its machinability rates fair (35/100) against not recommended (10/100) for 85 QT-50-55HRC.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 85-N and 85 QT-50-55HRC side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.