Steel 8115-ANN vs 8115-N
Steel · 8115 temper comparison
8115-ANN and 8115-N are two conditions of the same steel grade, 8115: ANN (annealed) versus N (normalized). The chemistry is identical, so every difference below comes from the condition. 8115-N is the stronger of the two: yield strength 370 MPa (53.7 ksi) against 310 MPa (45 ksi) for 8115-ANN, about 19% more; tensile strength follows at 560 MPa (81.2 ksi) vs 480 MPa (69.6 ksi). In exchange, 8115-ANN is the more ductile: elongation 32% versus 28% for 8115-N, and 8115-N is harder (163 HB vs 137 HB).
8115-ANNChoose it when the part is bent, formed or impact-loaded.
8115-NChoose it when strength drives the design.
8115-ANN vs 8115-N: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Same in both: Elastic (Young's) Modulus 205 GPa29.7 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29 · Compressive Strength 310 MPa45 ksi · Fracture Toughness (K_IC) 100 MPa·√m91 ksi·√in
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,425°C2,597 °F · Liquidus Temperature 1,500°C2,732 °F
Thermal
How each material carries heat and how hot it can run.
Same in both: Thermal Conductivity 44 W/m·K25.4 BTU/hr·ft·°F · Specific Heat Capacity 475 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 11.5 µm/m·K6.4 µin/in·°F · Latent Heat of Fusion 250 J/g107 BTU/lb · Max Service Temperature (continuous) 350°C662 °F · Min Service Temperature -40°C-40 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 7.8 % IACS · Electrical Resistivity 2.2×10⁻⁷ Ω·m8.66 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.62 V · Corrosion Resistance 12 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Same in both: Weldability 65 / 100 · Formability (cold) 65 / 100 · Brazeability / Solderability 60 / 100 · Polishability 60 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 26 MJ/kg11,178 BTU/lb · Embodied Carbon (primary production) 1.9 kg CO₂/kg · Embodied Water 55 L/kg6.6 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
8115-ANN vs 8115-N — frequently asked
Is 8115-N stronger than 8115-ANN?
Yes. 8115-N has a typical yield strength of 370 MPa (53.7 ksi) against 310 MPa (45 ksi) for 8115-ANN — about 19% more. Tensile strength is 560 MPa (81.2 ksi) vs 480 MPa (69.6 ksi).
Which condition does FabDigit quote by default, ANN or N?
ANN is the default 8115 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose 8115-ANN over 8115-N?
Pick 8115-ANN when the part is bent, formed or impact-loaded. Pick 8115-N when strength drives the design.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 8115-ANN and 8115-N side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.