Steel 5CrNiMo Normalized vs 5CrNiMo QT44-48
Steel · 5CrNiMo temper comparison
5CrNiMo Normalized and 5CrNiMo QT44-48 are two conditions of the same steel grade, 5CrNiMo: Normalized versus QT44-48 (Q&T 44–48 HRC). The chemistry is identical, so every difference below comes from the condition. 5CrNiMo QT44-48 is the stronger of the two: yield strength 1,300 MPa (189 ksi) against 620 MPa (89.9 ksi) for 5CrNiMo Normalized, about 110% more; tensile strength follows at 1,500 MPa (218 ksi) vs 1,000 MPa (145 ksi). In exchange, 5CrNiMo Normalized is the more ductile: elongation 12% versus 8% for 5CrNiMo QT44-48, and 5CrNiMo Normalized is harder (300 HB vs 220 HB). 5CrNiMo QT44-48 runs hotter in service (350°C vs 300°C continuous). On the shop floor, 5CrNiMo Normalized machines more easily (fair vs poor).
5CrNiMo NormalizedChoose it when the part is bent, formed or impact-loaded, or when the part is machined in volume.
5CrNiMo QT44-48Choose it when strength drives the design, or when the part sees heat.
5CrNiMo Normalized vs 5CrNiMo QT44-48: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
5CrNiMo Normalized5CrNiMo QT44-48
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 210 GPa30.5 Msi · Shear Modulus 81 GPa11.7 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.3
Physical
Density and transition temperatures.
Same in both: Density 7.83 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,420°C2,588 °F · Liquidus Temperature 1,480°C2,696 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 33 W/m·K19.1 BTU/hr·ft·°F · Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 12.5 µm/m·K6.9 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Min Service Temperature -30°C-22 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Resistivity 2.6×10⁻⁷ Ω·m10.2 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Corrosion Resistance 12 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Polishability 55 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 32 MJ/kg13,758 BTU/lb · Embodied Carbon (primary production) 2.4 kg CO₂/kg · Embodied Water 60 L/kg7.2 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
5CrNiMo Normalized vs 5CrNiMo QT44-48 — frequently asked
Is 5CrNiMo QT44-48 stronger than 5CrNiMo Normalized?
Yes. 5CrNiMo QT44-48 has a typical yield strength of 1,300 MPa (189 ksi) against 620 MPa (89.9 ksi) for 5CrNiMo Normalized — about 110% more. Tensile strength is 1,500 MPa (218 ksi) vs 1,000 MPa (145 ksi).
Which condition does FabDigit quote by default, Normalized or QT44-48?
Annealed is the default 5CrNiMo condition in the FabDigit quote flow (neither Normalized nor QT44-48). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 5CrNiMo Normalized or 5CrNiMo QT44-48?
5CrNiMo Normalized. Its machinability rates fair (40/100) against poor (15/100) for 5CrNiMo QT44-48; for welding the order is 5CrNiMo QT44-48 first (poor, 30/100) then 5CrNiMo Normalized (poor, 25/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 5CrNiMo Normalized and 5CrNiMo QT44-48 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.