Steel 56SiCr7 +A vs 56SiCr7 +C
Steel · 56SiCr7 temper comparison
56SiCr7 +A and 56SiCr7 +C are two conditions of the same steel grade, 56SiCr7: +A (annealed) versus +C (cold drawn). The chemistry is identical, so every difference below comes from the condition. 56SiCr7 +C is the stronger of the two: yield strength 800 MPa (116 ksi) against 470 MPa (68.2 ksi) for 56SiCr7 +A, about 70% more; tensile strength follows at 1,000 MPa (145 ksi) vs 820 MPa (119 ksi). In exchange, 56SiCr7 +A is the more ductile: elongation 15% versus 8% for 56SiCr7 +C, and 56SiCr7 +C is harder (31 HRC vs 21 HRC). 56SiCr7 +A runs hotter in service (300°C vs 200°C continuous).
56SiCr7 +AChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
56SiCr7 +CChoose it when strength drives the design.
56SiCr7 +A vs 56SiCr7 +C: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Rockwell C
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 200 GPa29 Msi · Shear Modulus 78.5 GPa11.4 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Same in both: Density 7.75 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,400°C2,552 °F · Liquidus Temperature 1,470°C2,678 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 30 W/m·K17.3 BTU/hr·ft·°F · Specific Heat Capacity 470 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 11.5 µm/m·K6.4 µin/in·°F · Latent Heat of Fusion 250 J/g107 BTU/lb · Min Service Temperature -40°C-40 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 4.9 % IACS · Electrical Resistivity 3.5×10⁻⁷ Ω·m13.8 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.6 V · Corrosion Resistance 11 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 40 / 100 · Brazeability / Solderability 30 / 100 · Polishability 60 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 28 MJ/kg12,038 BTU/lb · Embodied Carbon (primary production) 2 kg CO₂/kg · Embodied Water 60 L/kg7.2 gal/lb · Typical Recycled Content 25%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
56SiCr7 +A vs 56SiCr7 +C — frequently asked
Is 56SiCr7 +C stronger than 56SiCr7 +A?
Yes. 56SiCr7 +C has a typical yield strength of 800 MPa (116 ksi) against 470 MPa (68.2 ksi) for 56SiCr7 +A — about 70% more. Tensile strength is 1,000 MPa (145 ksi) vs 820 MPa (119 ksi).
Which condition does FabDigit quote by default, +A or +C?
+QT is the default 56SiCr7 condition in the FabDigit quote flow (neither +A nor +C). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which welds better, 56SiCr7 +A or 56SiCr7 +C?
56SiCr7 +A. Its weldability rates poor (20/100) against not recommended (12/100) for 56SiCr7 +C.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 56SiCr7 +A and 56SiCr7 +C side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.