Steel 4J42 Annealed vs 4J42-CD
Steel · 4J42 temper comparison
4J42 Annealed and 4J42-CD are two conditions of the same steel grade, 4J42: Annealed versus CD (cold drawn). The chemistry is identical, so every difference below comes from the condition. 4J42-CD is the stronger of the two: yield strength 490 MPa (71.1 ksi) against 285 MPa (41.3 ksi) for 4J42 Annealed, about 72% more; tensile strength follows at 630 MPa (91.4 ksi) vs 510 MPa (74 ksi). In exchange, 4J42 Annealed is the more ductile: elongation 35% versus 15% for 4J42-CD, and 4J42-CD is harder (190 HB vs 145 HB). 4J42 Annealed runs hotter in service (400°C vs 300°C continuous). On the shop floor, 4J42-CD machines more easily (45 vs 35 out of 100).
4J42 AnnealedChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
4J42-CDChoose it when strength drives the design, or when the part is machined in volume.
4J42 Annealed vs 4J42-CD: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 145 GPa21 Msi · Shear Modulus 57 GPa8.3 Msi · Bulk Modulus 106 GPa15.4 Msi · Poisson's Ratio 0.28
Physical
Density and transition temperatures.
Same in both: Density 8.12 g/cm³0.29 lb/in³ · Melting Point (Solidus) 1,425°C2,597 °F · Liquidus Temperature 1,450°C2,642 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 12.6 W/m·K7.3 BTU/hr·ft·°F · Specific Heat Capacity 500 J/kg·K0.12 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 5.3 µm/m·K2.9 µin/in·°F · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.4 V · Corrosion Resistance 28 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 80 / 100 · Polishability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 70 MJ/kg30,095 BTU/lb · Embodied Carbon (primary production) 6.6 kg CO₂/kg · Embodied Water 110 L/kg13.2 gal/lb · Typical Recycled Content 35%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
4J42 Annealed vs 4J42-CD — frequently asked
Is 4J42-CD stronger than 4J42 Annealed?
Yes. 4J42-CD has a typical yield strength of 490 MPa (71.1 ksi) against 285 MPa (41.3 ksi) for 4J42 Annealed — about 72% more. Tensile strength is 630 MPa (91.4 ksi) vs 510 MPa (74 ksi).
Which condition does FabDigit quote by default, Annealed or CD?
Annealed is the default 4J42 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 4J42 Annealed or 4J42-CD?
4J42-CD, by a small margin. Both rate fair for machinability — 45/100 against 35/100 for 4J42 Annealed; for welding the order is 4J42 Annealed first (very good, 70/100) then 4J42-CD (good, 65/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 4J42 Annealed and 4J42-CD side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.