Steel 4Cr5MoSiV1 QT 44-46HRC vs 4Cr5MoSiV1 QT 50-54HRC
Steel · 4Cr5MoSiV1 temper comparison
4Cr5MoSiV1 QT 44-46HRC and 4Cr5MoSiV1 QT 50-54HRC are two conditions of the same steel grade, 4Cr5MoSiV1: QT 44-46HRC versus QT 50-54HRC. The chemistry is identical, so every difference below comes from the condition. 4Cr5MoSiV1 QT 50-54HRC is the stronger of the two: yield strength 1,650 MPa (239 ksi) against 1,300 MPa (189 ksi) for 4Cr5MoSiV1 QT 44-46HRC, about 27% more; tensile strength follows at 1,960 MPa (284 ksi) vs 1,500 MPa (218 ksi). In exchange, 4Cr5MoSiV1 QT 44-46HRC is the more ductile: elongation 11% versus 6% for 4Cr5MoSiV1 QT 50-54HRC, and 4Cr5MoSiV1 QT 44-46HRC is harder (421 HB vs 210 HB). On the shop floor, 4Cr5MoSiV1 QT 44-46HRC machines more easily (poor vs not recommended).
4Cr5MoSiV1 QT 44-46HRCChoose it when the part is bent, formed or impact-loaded, or when the part is machined in volume.
4Cr5MoSiV1 QT 50-54HRCChoose it when strength drives the design.
4Cr5MoSiV1 QT 44-46HRC vs 4Cr5MoSiV1 QT 50-54HRC: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
4Cr5MoSiV1 QT 44-46HRC4Cr5MoSiV1 QT 50-54HRC
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 210 GPa30.5 Msi · Shear Modulus 81 GPa11.7 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.3 · Hardness, Rockwell B 95 HRB
Physical
Density and transition temperatures.
Same in both: Density 7.8 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,315°C2,399 °F · Liquidus Temperature 1,454°C2,649 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 26 W/m·K15 BTU/hr·ft·°F · Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 10.9 µm/m·K6.1 µin/in·°F · Latent Heat of Fusion 250 J/g107 BTU/lb · Min Service Temperature -30°C-22 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 3.3 % IACS · Electrical Resistivity 5.2×10⁻⁷ Ω·m20.5 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.55 V · Corrosion Resistance 20 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Polishability
Same in both: Weldability 40 / 100 · Formability (cold) 25 / 100 · Castability 30 / 100 · Brazeability / Solderability 35 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 36 MJ/kg15,477 BTU/lb · Embodied Carbon (primary production) 2.9 kg CO₂/kg · Embodied Water 80 L/kg9.6 gal/lb · Typical Recycled Content 40%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
4Cr5MoSiV1 QT 44-46HRC vs 4Cr5MoSiV1 QT 50-54HRC — frequently asked
Is 4Cr5MoSiV1 QT 50-54HRC stronger than 4Cr5MoSiV1 QT 44-46HRC?
Yes. 4Cr5MoSiV1 QT 50-54HRC has a typical yield strength of 1,650 MPa (239 ksi) against 1,300 MPa (189 ksi) for 4Cr5MoSiV1 QT 44-46HRC — about 27% more. Tensile strength is 1,960 MPa (284 ksi) vs 1,500 MPa (218 ksi).
Which condition does FabDigit quote by default, QT 44-46HRC or QT 50-54HRC?
ANN is the default 4Cr5MoSiV1 condition in the FabDigit quote flow (neither QT 44-46HRC nor QT 50-54HRC). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 4Cr5MoSiV1 QT 44-46HRC or 4Cr5MoSiV1 QT 50-54HRC?
4Cr5MoSiV1 QT 44-46HRC. Its machinability rates poor (24/100) against not recommended (12/100) for 4Cr5MoSiV1 QT 50-54HRC.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 4Cr5MoSiV1 QT 44-46HRC and 4Cr5MoSiV1 QT 50-54HRC side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.