Steel 41CrS4 +A vs 41CrS4 +H
Steel · 41CrS4 temper comparison
41CrS4 +A and 41CrS4 +H are two conditions of the same steel grade, 41CrS4: +A (annealed) versus +H (supplied with specified (standard) hardenability band; typically…). The chemistry is identical, so every difference below comes from the condition. 41CrS4 +H is the stronger of the two: yield strength 1,500 MPa (218 ksi) against 420 MPa (60.9 ksi) for 41CrS4 +A, about 3.6 times as much; tensile strength follows at 1,950 MPa (283 ksi) vs 680 MPa (98.6 ksi). In exchange, 41CrS4 +A is the more ductile: elongation 20% versus 2% for 41CrS4 +H, and 41CrS4 +H is harder (600 HB vs 205 HB). 41CrS4 +A runs hotter in service (400°C vs 180°C continuous). On the shop floor, 41CrS4 +A machines more easily (good vs not recommended) and 41CrS4 +A welds better (poor vs not recommended).
41CrS4 +AChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
41CrS4 +HChoose it when strength drives the design.
41CrS4 +A vs 41CrS4 +H: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell C
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 210 GPa30.5 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29 · Compressive Strength 730 MPa106 ksi · Shear Strength 590 MPa85.6 ksi
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,420°C2,588 °F · Liquidus Temperature 1,490°C2,714 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 44 W/m·K25.4 BTU/hr·ft·°F · Specific Heat Capacity 465 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 12 µm/m·K6.7 µin/in·°F · Latent Heat of Fusion 250 J/g107 BTU/lb · Min Service Temperature -20°C-4 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 7.7 % IACS · Electrical Resistivity 2.2×10⁻⁷ Ω·m8.66 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.65 V · Corrosion Resistance 12 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 40 / 100 · Brazeability / Solderability 55 / 100 · Polishability 55 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 27 MJ/kg11,608 BTU/lb · Embodied Carbon (primary production) 2.1 kg CO₂/kg · Embodied Water 60 L/kg7.2 gal/lb · Typical Recycled Content 35%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
41CrS4 +A vs 41CrS4 +H — frequently asked
Is 41CrS4 +H stronger than 41CrS4 +A?
Yes. 41CrS4 +H has a typical yield strength of 1,500 MPa (218 ksi) against 420 MPa (60.9 ksi) for 41CrS4 +A — about 3.6 times as much. Tensile strength is 1,950 MPa (283 ksi) vs 680 MPa (98.6 ksi).
Which condition does FabDigit quote by default, +A or +H?
+QT 16-40 is the default 41CrS4 condition in the FabDigit quote flow (neither +A nor +H). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 41CrS4 +A or 41CrS4 +H?
41CrS4 +A. Its machinability rates good (65/100) against not recommended (12/100) for 41CrS4 +H; for welding the order is 41CrS4 +A first (poor, 25/100) then 41CrS4 +H (not recommended, 10/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 41CrS4 +A and 41CrS4 +H side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.