Steel 4161-QT205 vs 4161-QT425
Steel · 4161 temper comparison
4161-QT205 and 4161-QT425 are two conditions of the same steel grade, 4161: QT205 (Q&T 205 °C) versus QT425 (Q&T 425 °C). The chemistry is identical, so every difference below comes from the condition. 4161-QT205 is the stronger of the two: yield strength 1,725 MPa (250 ksi) against 1,415 MPa (205 ksi) for 4161-QT425, about 22% more; tensile strength follows at 2,035 MPa (295 ksi) vs 1,550 MPa (225 ksi). In exchange, 4161-QT425 is the more ductile: elongation 11% versus 6% for 4161-QT205, and 4161-QT205 is harder (600 HB vs 430 HB). 4161-QT425 runs hotter in service (350°C vs 150°C continuous). On the shop floor, 4161-QT425 machines more easily (27 vs 15 out of 100) and 4161-QT425 welds better (poor vs not recommended).
4161-QT205Choose it when strength drives the design.
4161-QT425Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
4161-QT205 vs 4161-QT425: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 205 GPa29.7 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29 · Hardness, Rockwell B 96 HRB
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,416°C2,581 °F · Liquidus Temperature 1,465°C2,669 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 42.7 W/m·K24.7 BTU/hr·ft·°F · Specific Heat Capacity 475 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 12.3 µm/m·K6.8 µin/in·°F · Latent Heat of Fusion 250 J/g107 BTU/lb · Min Service Temperature -30°C-22 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 7.8 % IACS · Electrical Resistivity 2.2×10⁻⁷ Ω·m8.66 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.61 V · Corrosion Resistance 11 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Same in both: Formability (cold) 35 / 100 · Brazeability / Solderability 55 / 100 · Polishability 60 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 30 MJ/kg12,898 BTU/lb · Embodied Carbon (primary production) 2.2 kg CO₂/kg · Embodied Water 55 L/kg6.6 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
4161-QT205 vs 4161-QT425 — frequently asked
Is 4161-QT205 stronger than 4161-QT425?
Yes. 4161-QT205 has a typical yield strength of 1,725 MPa (250 ksi) against 1,415 MPa (205 ksi) for 4161-QT425 — about 22% more. Tensile strength is 2,035 MPa (295 ksi) vs 1,550 MPa (225 ksi).
Which condition does FabDigit quote by default, QT205 or QT425?
A is the default 4161 condition in the FabDigit quote flow (neither QT205 nor QT425). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 4161-QT205 or 4161-QT425?
4161-QT425, by a small margin. Both rate poor for machinability — 27/100 against 15/100 for 4161-QT205; for welding the order is 4161-QT425 first (poor, 20/100) then 4161-QT205 (not recommended, 10/100).