Steel 4135-CR vs 4135 Normalized
Steel · 4135 temper comparison
4135-CR and 4135 Normalized are two conditions of the same steel grade, 4135: CR (cold rolled) versus Normalized. The chemistry is identical, so every difference below comes from the condition. 4135-CR is the stronger of the two: yield strength 620 MPa (89.9 ksi) against 570 MPa (82.7 ksi) for 4135 Normalized, about 9% more. In exchange, 4135 Normalized is the more ductile: elongation 20% versus 11% for 4135-CR, and 4135 Normalized is harder (250 HB vs 225 HB). 4135 Normalized runs hotter in service (400°C vs 300°C continuous).
4135-CRChoose it when strength drives the design.
4135 NormalizedChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
4135-CR vs 4135 Normalized: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 205 GPa29.7 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,416°C2,581 °F · Liquidus Temperature 1,480°C2,696 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 42 W/m·K24.3 BTU/hr·ft·°F · Specific Heat Capacity 477 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 12.3 µm/m·K6.8 µin/in·°F · Latent Heat of Fusion 247 J/g106 BTU/lb · Min Service Temperature -40°C-40 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 7.8 % IACS · Electrical Resistivity 2.2×10⁻⁷ Ω·m8.66 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.6 V · Corrosion Resistance 12 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 60 / 100 · Polishability 65 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 34 MJ/kg14,617 BTU/lb · Embodied Carbon (primary production) 2.3 kg CO₂/kg · Embodied Water 45 L/kg5.4 gal/lb · Typical Recycled Content 25%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
4135-CR vs 4135 Normalized — frequently asked
Is 4135-CR stronger than 4135 Normalized?
Yes. 4135-CR has a typical yield strength of 620 MPa (89.9 ksi) against 570 MPa (82.7 ksi) for 4135 Normalized — about 9% more. Tensile strength is 760 MPa (110 ksi) vs 860 MPa (125 ksi).
Which condition does FabDigit quote by default, CR or Normalized?
HR is the default 4135 condition in the FabDigit quote flow (neither CR nor Normalized). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 4135-CR or 4135 Normalized?
4135-CR. Its machinability rates good (58/100) against fair (52/100) for 4135 Normalized.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 4135-CR and 4135 Normalized side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.