Steel 38CrMoAlA Annealed vs 38CrMoAlA-CD
Steel · 38CrMoAlA temper comparison
38CrMoAlA Annealed and 38CrMoAlA-CD are two conditions of the same steel grade, 38CrMoAlA: Annealed versus CD (cold drawn). The chemistry is identical, so every difference below comes from the condition. 38CrMoAlA-CD is the stronger of the two: yield strength 700 MPa (102 ksi) against 450 MPa (65.3 ksi) for 38CrMoAlA Annealed, about 56% more; tensile strength follows at 850 MPa (123 ksi) vs 720 MPa (104 ksi). In exchange, 38CrMoAlA Annealed is the more ductile: elongation 20% versus 10% for 38CrMoAlA-CD, and 38CrMoAlA-CD is harder (255 HB vs 210 HB). 38CrMoAlA Annealed runs hotter in service (500°C vs 350°C continuous).
38CrMoAlA AnnealedChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
38CrMoAlA-CDChoose it when strength drives the design.
38CrMoAlA Annealed vs 38CrMoAlA-CD: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
38CrMoAlA Annealed38CrMoAlA-CD
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell C
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 210 GPa30.5 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Same in both: Density 7.8 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,420°C2,588 °F · Liquidus Temperature 1,490°C2,714 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 470 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 11.9 µm/m·K6.6 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Min Service Temperature -40°C-40 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.6 V · Corrosion Resistance 12 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 25 / 100 · Brazeability / Solderability 35 / 100 · Polishability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 34 MJ/kg14,617 BTU/lb · Embodied Carbon (primary production) 2.3 kg CO₂/kg · Embodied Water 55 L/kg6.6 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
38CrMoAlA Annealed vs 38CrMoAlA-CD — frequently asked
Is 38CrMoAlA-CD stronger than 38CrMoAlA Annealed?
Yes. 38CrMoAlA-CD has a typical yield strength of 700 MPa (102 ksi) against 450 MPa (65.3 ksi) for 38CrMoAlA Annealed — about 56% more. Tensile strength is 850 MPa (123 ksi) vs 720 MPa (104 ksi).
Which condition does FabDigit quote by default, Annealed or CD?
Q&T is the default 38CrMoAlA condition in the FabDigit quote flow (neither Annealed nor CD). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 38CrMoAlA Annealed or 38CrMoAlA-CD?
38CrMoAlA Annealed. Its machinability rates good (55/100) against fair (50/100) for 38CrMoAlA-CD; for welding the order is 38CrMoAlA Annealed first (poor, 25/100) then 38CrMoAlA-CD (poor, 20/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 38CrMoAlA Annealed and 38CrMoAlA-CD side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.