Steel 38B2 +A vs 38B2 +H
Steel · 38B2 temper comparison
38B2 +A and 38B2 +H are two conditions of the same steel grade, 38B2: +A (annealed) versus +H (hardened). The chemistry is identical, so every difference below comes from the condition. 38B2 +H is the stronger of the two: yield strength 1,400 MPa (203 ksi) against 330 MPa (47.9 ksi) for 38B2 +A, about 4.2 times as much; tensile strength follows at 1,900 MPa (276 ksi) vs 560 MPa (81.2 ksi). In exchange, 38B2 +A is the more ductile: elongation 23% versus 3% for 38B2 +H, and 38B2 +H is harder (540 HB vs 165 HB). 38B2 +A runs hotter in service (350°C vs 150°C continuous). On the shop floor, 38B2 +A welds better (fair vs poor).
38B2 +AChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
38B2 +HChoose it when strength drives the design.
38B2 +A vs 38B2 +H: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Same in both: Elastic (Young's) Modulus 210 GPa30.5 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,425°C2,597 °F · Liquidus Temperature 1,495°C2,723 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 470 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 11.9 µm/m·K6.6 µin/in·°F · Latent Heat of Fusion 250 J/g107 BTU/lb · Min Service Temperature -30°C-22 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.61 V · Corrosion Resistance 10 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 60 / 100 · Polishability 55 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 25 MJ/kg10,748 BTU/lb · Embodied Carbon (primary production) 2 kg CO₂/kg · Embodied Water 55 L/kg6.6 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
38B2 +A vs 38B2 +H — frequently asked
Is 38B2 +H stronger than 38B2 +A?
Yes. 38B2 +H has a typical yield strength of 1,400 MPa (203 ksi) against 330 MPa (47.9 ksi) for 38B2 +A — about 4.2 times as much. Tensile strength is 1,900 MPa (276 ksi) vs 560 MPa (81.2 ksi).
Which condition does FabDigit quote by default, +A or +H?
+AC+C is the default 38B2 condition in the FabDigit quote flow (neither +A nor +H). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 38B2 +A or 38B2 +H?
38B2 +A, by a small margin. Both rate good for machinability — 62/100 against 55/100 for 38B2 +H; for welding the order is 38B2 +A first (fair, 45/100) then 38B2 +H (poor, 15/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 38B2 +A and 38B2 +H side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.