Steel 31CrMo12 +A vs 31CrMo12 +QT
Steel · 31CrMo12 temper comparison
31CrMo12 +A and 31CrMo12 +QT are two conditions of the same steel grade, 31CrMo12: +A (annealed) versus +QT (quenched and tempered). The chemistry is identical, so every difference below comes from the condition. 31CrMo12 +QT is the stronger of the two: yield strength 900 MPa (131 ksi) against 470 MPa (68.2 ksi) for 31CrMo12 +A, about 91% more; tensile strength follows at 1,100 MPa (160 ksi) vs 800 MPa (116 ksi). In exchange, 31CrMo12 +A is the more ductile: elongation 18% versus 13% for 31CrMo12 +QT, and 31CrMo12 +QT is harder (340 HB vs 230 HB). On the shop floor, 31CrMo12 +A machines more easily (good vs fair) and 31CrMo12 +A welds better (fair vs poor).
31CrMo12 +AChoose it when the part is bent, formed or impact-loaded, or when the part is machined in volume.
31CrMo12 +QTChoose it when strength drives the design.
31CrMo12 +A vs 31CrMo12 +QT: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Same in both: Elastic (Young's) Modulus 210 GPa30.5 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29 · Compressive Strength 900 MPa131 ksi · Shear Strength 660 MPa95.7 ksi · Fracture Toughness (K_IC) 70 MPa·√m63.7 ksi·√in · Hardness, Rockwell C 35 HRC · Hardness, Vickers 355 HV
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,420°C2,588 °F · Liquidus Temperature 1,490°C2,714 °F
Thermal
How each material carries heat and how hot it can run.
Same in both: Thermal Conductivity 34 W/m·K19.6 BTU/hr·ft·°F · Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 12.2 µm/m·K6.8 µin/in·°F · Latent Heat of Fusion 250 J/g107 BTU/lb · Max Service Temperature (continuous) 480°C896 °F · Min Service Temperature -40°C-40 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 6.6 % IACS · Electrical Resistivity 2.6×10⁻⁷ Ω·m10.2 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.6 V · Corrosion Resistance 15 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 40 / 100 · Polishability 60 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 34 MJ/kg14,617 BTU/lb · Embodied Carbon (primary production) 2.3 kg CO₂/kg · Embodied Water 60 L/kg7.2 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
31CrMo12 +A vs 31CrMo12 +QT — frequently asked
Is 31CrMo12 +QT stronger than 31CrMo12 +A?
Yes. 31CrMo12 +QT has a typical yield strength of 900 MPa (131 ksi) against 470 MPa (68.2 ksi) for 31CrMo12 +A — about 91% more. Tensile strength is 1,100 MPa (160 ksi) vs 800 MPa (116 ksi).
Which condition does FabDigit quote by default, +A or +QT?
+QT is the default 31CrMo12 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 31CrMo12 +A or 31CrMo12 +QT?
31CrMo12 +A. Its machinability rates good (55/100) against fair (40/100) for 31CrMo12 +QT; for welding the order is 31CrMo12 +A first (fair, 35/100) then 31CrMo12 +QT (poor, 25/100).