Steel 2316 Nitrided vs 2316 Q&T
Steel · 2316 temper comparison
2316 Nitrided and 2316 Q&T are two conditions of the same steel grade, 2316: Nitrided versus Q&T (quenched and tempered). The chemistry is identical, so every difference below comes from the condition. 2316 Q&T is the stronger of the two: yield strength 1,350 MPa (196 ksi) against 850 MPa (123 ksi) for 2316 Nitrided, about 59% more; tensile strength follows at 1,600 MPa (232 ksi) vs 1,020 MPa (148 ksi). In exchange, 2316 Nitrided is the more ductile: elongation 10% versus 5% for 2316 Q&T, and 2316 Q&T is harder (460 HB vs 300 HB). 2316 Nitrided runs hotter in service (450°C vs 200°C continuous). On the shop floor, 2316 Q&T machines more easily (poor vs not recommended) and 2316 Q&T welds better (poor vs not recommended).
2316 NitridedChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
2316 Q&TChoose it when strength drives the design, or when the part is machined in volume.
2316 Nitrided vs 2316 Q&T: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell C
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 215 GPa31.2 Msi · Shear Modulus 82 GPa11.9 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29 · Compressive Strength 900 MPa131 ksi · Shear Strength 620 MPa89.9 ksi
Physical
Density and transition temperatures.
Same in both: Density 7.7 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,420°C2,588 °F · Liquidus Temperature 1,480°C2,696 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 20 W/m·K11.6 BTU/hr·ft·°F · Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 10.5 µm/m·K5.8 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Min Service Temperature -20°C-4 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 2.7 % IACS · Electrical Resistivity 6.5×10⁻⁷ Ω·m25.6 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.3 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Polishability
Same in both: Castability 25 / 100 · Brazeability / Solderability 30 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 42 MJ/kg18,057 BTU/lb · Embodied Carbon (primary production) 3.4 kg CO₂/kg · Embodied Water 80 L/kg9.6 gal/lb · Typical Recycled Content 45%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
2316 Nitrided vs 2316 Q&T — frequently asked
Is 2316 Q&T stronger than 2316 Nitrided?
Yes. 2316 Q&T has a typical yield strength of 1,350 MPa (196 ksi) against 850 MPa (123 ksi) for 2316 Nitrided — about 59% more. Tensile strength is 1,600 MPa (232 ksi) vs 1,020 MPa (148 ksi).
Which condition does FabDigit quote by default, Nitrided or Q&T?
Annealed is the default 2316 condition in the FabDigit quote flow (neither Nitrided nor Q&T). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 2316 Nitrided or 2316 Q&T?
2316 Q&T. Its machinability rates poor (20/100) against not recommended (10/100) for 2316 Nitrided; for welding the order is 2316 Q&T first (poor, 30/100) then 2316 Nitrided (not recommended, 5/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 2316 Nitrided and 2316 Q&T side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.