Steel 20NiCrMo2-2 +AC vs 20NiCrMo2-2 +H
Steel · 20NiCrMo2-2 temper comparison
20NiCrMo2-2 +AC and 20NiCrMo2-2 +H are two conditions of the same steel grade, 20NiCrMo2-2: +AC (spheroidize annealed) versus +H (hardenability-controlled bar, hardened and tempered). The chemistry is identical, so every difference below comes from the condition. 20NiCrMo2-2 +H is the stronger of the two: yield strength 800 MPa (116 ksi) against 320 MPa (46.4 ksi) for 20NiCrMo2-2 +AC, about 150% more; tensile strength follows at 1,100 MPa (160 ksi) vs 510 MPa (74 ksi). In exchange, 20NiCrMo2-2 +AC is the more ductile: elongation 24% versus 12% for 20NiCrMo2-2 +H, and 20NiCrMo2-2 +H is harder (335 HB vs 160 HB). 20NiCrMo2-2 +AC runs hotter in service (350°C vs 200°C continuous). On the shop floor, 20NiCrMo2-2 +AC machines more easily (good vs fair) and 20NiCrMo2-2 +AC welds better (good vs fair).
20NiCrMo2-2 +ACChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
20NiCrMo2-2 +HChoose it when strength drives the design.
20NiCrMo2-2 +AC vs 20NiCrMo2-2 +H: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Same in both: Elastic (Young's) Modulus 207 GPa30 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,420°C2,588 °F · Liquidus Temperature 1,490°C2,714 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 44 W/m·K25.4 BTU/hr·ft·°F · Specific Heat Capacity 475 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 11.6 µm/m·K6.4 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Min Service Temperature -40°C-40 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 8 % IACS · Electrical Resistivity 2.2×10⁻⁷ Ω·m8.66 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.61 V · Corrosion Resistance 12 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 60 / 100 · Polishability 60 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 31 MJ/kg13,328 BTU/lb · Embodied Carbon (primary production) 2.2 kg CO₂/kg · Embodied Water 60 L/kg7.2 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
20NiCrMo2-2 +AC vs 20NiCrMo2-2 +H — frequently asked
Is 20NiCrMo2-2 +H stronger than 20NiCrMo2-2 +AC?
Yes. 20NiCrMo2-2 +H has a typical yield strength of 800 MPa (116 ksi) against 320 MPa (46.4 ksi) for 20NiCrMo2-2 +AC — about 150% more. Tensile strength is 1,100 MPa (160 ksi) vs 510 MPa (74 ksi).
Which condition does FabDigit quote by default, +AC or +H?
+FP is the default 20NiCrMo2-2 condition in the FabDigit quote flow (neither +AC nor +H). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 20NiCrMo2-2 +AC or 20NiCrMo2-2 +H?
20NiCrMo2-2 +AC. Its machinability rates good (58/100) against fair (38/100) for 20NiCrMo2-2 +H; for welding the order is 20NiCrMo2-2 +AC first (good, 58/100) then 20NiCrMo2-2 +H (fair, 35/100).