Steel 20MnVB-CD vs 20MnVB-QT200
Steel · 20MnVB temper comparison
20MnVB-CD and 20MnVB-QT200 are two conditions of the same steel grade, 20MnVB: CD (cold drawn) versus QT200 (860 °C oil quench + 200 °C temper). The chemistry is identical, so every difference below comes from the condition. 20MnVB-QT200 is the stronger of the two: yield strength 950 MPa (138 ksi) against 620 MPa (89.9 ksi) for 20MnVB-CD, about 53% more; tensile strength follows at 1,150 MPa (167 ksi) vs 750 MPa (109 ksi). 20MnVB-QT200 is harder — 360 HB against 225 HB for 20MnVB-CD — which matters for wear surfaces and threads. On the shop floor, 20MnVB-CD machines more easily (good vs fair), 20MnVB-CD welds better (45 vs 35 out of 100), and 20MnVB-CD forms better (30 vs 20 out of 100).
20MnVB-CDChoose it when the part is machined in volume, or when it will be welded.
20MnVB-QT200Choose it when strength drives the design, or when surface hardness matters.
20MnVB-CD vs 20MnVB-QT200: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell C
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 210 GPa30.5 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29 · Elongation at Break 12%
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,425°C2,597 °F · Liquidus Temperature 1,500°C2,732 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Same in both: Specific Heat Capacity 470 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 11.9 µm/m·K6.6 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Max Service Temperature (continuous) 200°C392 °F · Min Service Temperature -40°C-40 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 8 % IACS · Electrical Resistivity 2.2×10⁻⁷ Ω·m8.66 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.62 V · Corrosion Resistance 11 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 30 / 100 · Brazeability / Solderability 55 / 100 · Polishability 65 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 28 MJ/kg12,038 BTU/lb · Embodied Carbon (primary production) 2.1 kg CO₂/kg · Embodied Water 60 L/kg7.2 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
20MnVB-CD vs 20MnVB-QT200 — frequently asked
Is 20MnVB-QT200 stronger than 20MnVB-CD?
Yes. 20MnVB-QT200 has a typical yield strength of 950 MPa (138 ksi) against 620 MPa (89.9 ksi) for 20MnVB-CD — about 53% more. Tensile strength is 1,150 MPa (167 ksi) vs 750 MPa (109 ksi).
Which condition does FabDigit quote by default, CD or QT200?
QT200 is the default 20MnVB condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 20MnVB-CD or 20MnVB-QT200?
20MnVB-CD. Its machinability rates good (60/100) against fair (38/100) for 20MnVB-QT200; for welding the order is 20MnVB-CD first (fair, 45/100) then 20MnVB-QT200 (fair, 35/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 20MnVB-CD and 20MnVB-QT200 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.