Steel 20CrMo Annealed vs 20CrMo-CR
Steel · 20CrMo temper comparison
20CrMo Annealed and 20CrMo-CR are two conditions of the same steel grade, 20CrMo: Annealed versus CR (cold rolled). The chemistry is identical, so every difference below comes from the condition. 20CrMo-CR is the stronger of the two: yield strength 480 MPa (69.6 ksi) against 350 MPa (50.8 ksi) for 20CrMo Annealed, about 37% more; tensile strength follows at 640 MPa (92.8 ksi) vs 540 MPa (78.3 ksi). In exchange, 20CrMo Annealed is the more ductile: elongation 25% versus 14% for 20CrMo-CR, and 20CrMo-CR is harder (195 HB vs 170 HB). 20CrMo Annealed runs hotter in service (500°C vs 400°C continuous).
20CrMo AnnealedChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
20CrMo-CRChoose it when strength drives the design.
20CrMo Annealed vs 20CrMo-CR: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Same in both: Elastic (Young's) Modulus 210 GPa30.5 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,425°C2,597 °F · Liquidus Temperature 1,500°C2,732 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 42 W/m·K24.3 BTU/hr·ft·°F · Specific Heat Capacity 470 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 12.3 µm/m·K6.8 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Min Service Temperature -40°C-40 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Resistivity 2.3×10⁻⁷ Ω·m9.06 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Corrosion Resistance 13 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 60 / 100 · Polishability 60 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 30 MJ/kg12,898 BTU/lb · Embodied Carbon (primary production) 2.3 kg CO₂/kg · Embodied Water 45 L/kg5.4 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
20CrMo Annealed vs 20CrMo-CR — frequently asked
Is 20CrMo-CR stronger than 20CrMo Annealed?
Yes. 20CrMo-CR has a typical yield strength of 480 MPa (69.6 ksi) against 350 MPa (50.8 ksi) for 20CrMo Annealed — about 37% more. Tensile strength is 640 MPa (92.8 ksi) vs 540 MPa (78.3 ksi).
Which condition does FabDigit quote by default, Annealed or CR?
HR is the default 20CrMo condition in the FabDigit quote flow (neither Annealed nor CR). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 20CrMo Annealed or 20CrMo-CR?
20CrMo Annealed, by a small margin. Both rate good for machinability — 65/100 against 60/100 for 20CrMo-CR; for welding the order is 20CrMo Annealed first (good, 68/100) then 20CrMo-CR (good, 60/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 20CrMo Annealed and 20CrMo-CR side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.