Steel 18CrNi8-CR vs 18CrNi8 Q&T
Steel · 18CrNi8 temper comparison
18CrNi8-CR and 18CrNi8 Q&T are two conditions of the same steel grade, 18CrNi8: CR (cold rolled) versus Q&T (quenched and tempered). The chemistry is identical, so every difference below comes from the condition. 18CrNi8 Q&T is the stronger of the two: yield strength 830 MPa (120 ksi) against 690 MPa (100 ksi) for 18CrNi8-CR, about 20% more; tensile strength follows at 1,000 MPa (145 ksi) vs 860 MPa (125 ksi). 18CrNi8 Q&T is the more ductile: elongation 14% versus 9% for 18CrNi8-CR, and 18CrNi8 Q&T is harder (300 HB vs 250 HB). 18CrNi8 Q&T runs hotter in service (350°C vs 200°C continuous). On the shop floor, 18CrNi8-CR machines more easily (fair vs poor).
18CrNi8-CRChoose it when the part is machined in volume.
18CrNi8 Q&TChoose it when strength drives the design, or when the part is bent, formed or impact-loaded.
18CrNi8-CR vs 18CrNi8 Q&T: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell C
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 210 GPa30.5 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 165 GPa23.9 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,420°C2,588 °F · Liquidus Temperature 1,490°C2,714 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 34 W/m·K19.6 BTU/hr·ft·°F · Specific Heat Capacity 465 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 11.6 µm/m·K6.4 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Min Service Temperature -40°C-40 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 6.9 % IACS · Electrical Resistivity 2.5×10⁻⁷ Ω·m9.84 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Corrosion Resistance 12 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Same in both: Formability (cold) 35 / 100 · Brazeability / Solderability 55 / 100 · Polishability 65 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 33 MJ/kg14,187 BTU/lb · Embodied Carbon (primary production) 2.3 kg CO₂/kg · Embodied Water 55 L/kg6.6 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
18CrNi8-CR vs 18CrNi8 Q&T — frequently asked
Is 18CrNi8 Q&T stronger than 18CrNi8-CR?
Yes. 18CrNi8 Q&T has a typical yield strength of 830 MPa (120 ksi) against 690 MPa (100 ksi) for 18CrNi8-CR — about 20% more. Tensile strength is 1,000 MPa (145 ksi) vs 860 MPa (125 ksi).
Which condition does FabDigit quote by default, CR or Q&T?
HR is the default 18CrNi8 condition in the FabDigit quote flow (neither CR nor Q&T). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 18CrNi8-CR or 18CrNi8 Q&T?
18CrNi8-CR. Its machinability rates fair (45/100) against poor (30/100) for 18CrNi8 Q&T.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 18CrNi8-CR and 18CrNi8 Q&T side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.