Steel 17MnCr5 +AC vs 17MnCr5 +H
Steel · 17MnCr5 temper comparison
17MnCr5 +AC and 17MnCr5 +H are two conditions of the same steel grade, 17MnCr5: +AC (spheroidize annealed) versus +H (supplied with specified (standard) hardenability, Jominy-controlled). The chemistry is identical, so every difference below comes from the condition. 17MnCr5 +H is the stronger of the two: yield strength 400 MPa (58 ksi) against 340 MPa (49.3 ksi) for 17MnCr5 +AC, about 18% more; tensile strength follows at 640 MPa (92.8 ksi) vs 560 MPa (81.2 ksi). In exchange, 17MnCr5 +AC is the more ductile: elongation 25% versus 19% for 17MnCr5 +H, and 17MnCr5 +H is harder (190 HB vs 165 HB).
17MnCr5 +ACChoose it when the part is bent, formed or impact-loaded.
17MnCr5 +HChoose it when strength drives the design.
17MnCr5 +AC vs 17MnCr5 +H: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 210 GPa30.5 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,420°C2,588 °F · Liquidus Temperature 1,500°C2,732 °F
Thermal
How each material carries heat and how hot it can run.
Same in both: Thermal Conductivity 44 W/m·K25.4 BTU/hr·ft·°F · Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 11.5 µm/m·K6.4 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Max Service Temperature (continuous) 180°C356 °F · Min Service Temperature -30°C-22 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Resistivity 2.1×10⁻⁷ Ω·m8.27 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Corrosion Resistance 12 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 60 / 100 · Polishability 60 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 32 MJ/kg13,758 BTU/lb · Embodied Carbon (primary production) 2.2 kg CO₂/kg · Embodied Water 60 L/kg7.2 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
17MnCr5 +AC vs 17MnCr5 +H — frequently asked
Is 17MnCr5 +H stronger than 17MnCr5 +AC?
Yes. 17MnCr5 +H has a typical yield strength of 400 MPa (58 ksi) against 340 MPa (49.3 ksi) for 17MnCr5 +AC — about 18% more. Tensile strength is 640 MPa (92.8 ksi) vs 560 MPa (81.2 ksi).
Which condition does FabDigit quote by default, +AC or +H?
+A is the default 17MnCr5 condition in the FabDigit quote flow (neither +AC nor +H). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose 17MnCr5 +AC over 17MnCr5 +H?
Pick 17MnCr5 +AC when the part is bent, formed or impact-loaded. Pick 17MnCr5 +H when strength drives the design.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 17MnCr5 +AC and 17MnCr5 +H side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.