Steel 16MnCrS5 Annealed vs 16MnCrS5-CR
Steel · 16MnCrS5 temper comparison
16MnCrS5 Annealed and 16MnCrS5-CR are two conditions of the same steel grade, 16MnCrS5: Annealed versus CR (cold rolled). The chemistry is identical, so every difference below comes from the condition. 16MnCrS5-CR is the stronger of the two: yield strength 550 MPa (79.8 ksi) against 350 MPa (50.8 ksi) for 16MnCrS5 Annealed, about 57% more; tensile strength follows at 700 MPa (102 ksi) vs 560 MPa (81.2 ksi). In exchange, 16MnCrS5 Annealed is the more ductile: elongation 25% versus 12% for 16MnCrS5-CR, and 16MnCrS5-CR is harder (210 HB vs 165 HB). 16MnCrS5 Annealed runs hotter in service (180°C vs 150°C continuous).
16MnCrS5 AnnealedChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
16MnCrS5-CRChoose it when strength drives the design.
16MnCrS5 Annealed vs 16MnCrS5-CR: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Same in both: Elastic (Young's) Modulus 210 GPa30.5 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 165 GPa23.9 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,420°C2,588 °F · Liquidus Temperature 1,490°C2,714 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 11.5 µm/m·K6.4 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Min Service Temperature -25°C-13 °F
Electrical
Conductivity and insulation.
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.6 V · Corrosion Resistance 11 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 60 / 100 · Polishability 55 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 30 MJ/kg12,898 BTU/lb · Embodied Carbon (primary production) 2.1 kg CO₂/kg · Embodied Water 40 L/kg4.8 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
16MnCrS5 Annealed vs 16MnCrS5-CR — frequently asked
Is 16MnCrS5-CR stronger than 16MnCrS5 Annealed?
Yes. 16MnCrS5-CR has a typical yield strength of 550 MPa (79.8 ksi) against 350 MPa (50.8 ksi) for 16MnCrS5 Annealed — about 57% more. Tensile strength is 700 MPa (102 ksi) vs 560 MPa (81.2 ksi).
Which condition does FabDigit quote by default, Annealed or CR?
HR is the default 16MnCrS5 condition in the FabDigit quote flow (neither Annealed nor CR). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which welds better, 16MnCrS5 Annealed or 16MnCrS5-CR?
16MnCrS5 Annealed. Its weldability rates fair (48/100) against fair (42/100) for 16MnCrS5-CR.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 16MnCrS5 Annealed and 16MnCrS5-CR side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.