Steel 15MnMoV4-5 +A vs 15MnMoV4-5 +QT
Steel · 15MnMoV4-5 temper comparison
15MnMoV4-5 +A and 15MnMoV4-5 +QT are two conditions of the same steel grade, 15MnMoV4-5: +A (annealed) versus +QT (quenched and tempered). The chemistry is identical, so every difference below comes from the condition. 15MnMoV4-5 +QT is the stronger of the two: yield strength 550 MPa (79.8 ksi) against 330 MPa (47.9 ksi) for 15MnMoV4-5 +A, about 67% more; tensile strength follows at 720 MPa (104 ksi) vs 540 MPa (78.3 ksi). In exchange, 15MnMoV4-5 +A is the more ductile: elongation 26% versus 18% for 15MnMoV4-5 +QT, and 15MnMoV4-5 +QT is harder (225 HB vs 160 HB). 15MnMoV4-5 +QT runs hotter in service (480°C vs 400°C continuous). On the shop floor, 15MnMoV4-5 +A welds better (good vs fair).
15MnMoV4-5 +AChoose it when the part is bent, formed or impact-loaded, or when it will be welded.
15MnMoV4-5 +QTChoose it when strength drives the design, or when the part sees heat.
15MnMoV4-5 +A vs 15MnMoV4-5 +QT: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 210 GPa30.5 Msi · Shear Modulus 81 GPa11.7 Msi · Bulk Modulus 166 GPa24.1 Msi · Poisson's Ratio 0.29 · Fracture Toughness (K_IC) 120 MPa·√m109 ksi·√in
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,460°C2,660 °F · Liquidus Temperature 1,510°C2,750 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 465 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 12.3 µm/m·K6.8 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Min Service Temperature -20°C-4 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.62 V · Corrosion Resistance 12 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 40 / 100 · Brazeability / Solderability 55 / 100 · Polishability 55 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 31 MJ/kg13,328 BTU/lb · Embodied Carbon (primary production) 2.2 kg CO₂/kg · Embodied Water 55 L/kg6.6 gal/lb · Typical Recycled Content 25%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
15MnMoV4-5 +A vs 15MnMoV4-5 +QT — frequently asked
Is 15MnMoV4-5 +QT stronger than 15MnMoV4-5 +A?
Yes. 15MnMoV4-5 +QT has a typical yield strength of 550 MPa (79.8 ksi) against 330 MPa (47.9 ksi) for 15MnMoV4-5 +A — about 67% more. Tensile strength is 720 MPa (104 ksi) vs 540 MPa (78.3 ksi).
Which condition does FabDigit quote by default, +A or +QT?
+NT is the default 15MnMoV4-5 condition in the FabDigit quote flow (neither +A nor +QT). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 15MnMoV4-5 +A or 15MnMoV4-5 +QT?
15MnMoV4-5 +A, by a small margin. Both rate good for machinability — 63/100 against 55/100 for 15MnMoV4-5 +QT; for welding the order is 15MnMoV4-5 +A first (good, 60/100) then 15MnMoV4-5 +QT (fair, 50/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 15MnMoV4-5 +A and 15MnMoV4-5 +QT side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.