Steel 12KhN3A-A vs 12KhN3A-N
Steel · 12KhN3A temper comparison
12KhN3A-A and 12KhN3A-N are two conditions of the same steel grade, 12KhN3A: A (solution annealed) versus N (normalized). The chemistry is identical, so every difference below comes from the condition. 12KhN3A-N is the stronger of the two: yield strength 520 MPa (75.4 ksi) against 380 MPa (55.1 ksi) for 12KhN3A-A, about 37% more; tensile strength follows at 760 MPa (110 ksi) vs 620 MPa (89.9 ksi). In exchange, 12KhN3A-A is the more ductile: elongation 22% versus 18% for 12KhN3A-N, and 12KhN3A-N is harder (230 HB vs 200 HB). 12KhN3A-N runs hotter in service (350°C vs 200°C continuous).
12KhN3A-AChoose it when the part is bent, formed or impact-loaded.
12KhN3A-NChoose it when strength drives the design, or when the part sees heat.
12KhN3A-A vs 12KhN3A-N: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell C
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 210 GPa30.5 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,425°C2,597 °F · Liquidus Temperature 1,495°C2,723 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 470 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 11.4 µm/m·K6.3 µin/in·°F · Latent Heat of Fusion 250 J/g107 BTU/lb · Min Service Temperature -70°C-94 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.62 V · Corrosion Resistance 13 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 55 / 100 · Polishability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 34 MJ/kg14,617 BTU/lb · Embodied Carbon (primary production) 2.5 kg CO₂/kg · Embodied Water 60 L/kg7.2 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
12KhN3A-A vs 12KhN3A-N — frequently asked
Is 12KhN3A-N stronger than 12KhN3A-A?
Yes. 12KhN3A-N has a typical yield strength of 520 MPa (75.4 ksi) against 380 MPa (55.1 ksi) for 12KhN3A-A — about 37% more. Tensile strength is 760 MPa (110 ksi) vs 620 MPa (89.9 ksi).
Which condition does FabDigit quote by default, A or N?
QT is the default 12KhN3A condition in the FabDigit quote flow (neither A nor N). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 12KhN3A-A or 12KhN3A-N?
12KhN3A-A. Its machinability rates good (55/100) against fair (50/100) for 12KhN3A-N; for welding the order is 12KhN3A-A first (good, 55/100) then 12KhN3A-N (fair, 50/100).