Steel 12CrMoV12-10 +A vs 12CrMoV12-10 +QT+SPWHT
Steel · 12CrMoV12-10 temper comparison
12CrMoV12-10 +A and 12CrMoV12-10 +QT+SPWHT are two conditions of the same steel grade, 12CrMoV12-10: +A (annealed) versus +QT+SPWHT (+QT + simulated post-weld heat treatment). The chemistry is identical, so every difference below comes from the condition. 12CrMoV12-10 +QT+SPWHT is the stronger of the two: yield strength 460 MPa (66.7 ksi) against 350 MPa (50.8 ksi) for 12CrMoV12-10 +A, about 31% more; tensile strength follows at 630 MPa (91.4 ksi) vs 570 MPa (82.7 ksi). In exchange, 12CrMoV12-10 +A is the more ductile: elongation 24% versus 21% for 12CrMoV12-10 +QT+SPWHT, and 12CrMoV12-10 +QT+SPWHT is harder (195 HB vs 175 HB). 12CrMoV12-10 +QT+SPWHT runs hotter in service (540°C vs 450°C continuous).
12CrMoV12-10 +AChoose it when the part is bent, formed or impact-loaded.
12CrMoV12-10 +QT+SPWHTChoose it when strength drives the design, or when the part sees heat.
12CrMoV12-10 +A vs 12CrMoV12-10 +QT+SPWHT: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
12CrMoV12-10 +A12CrMoV12-10 +QT+SPWHT
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 210 GPa30.5 Msi · Shear Modulus 81 GPa11.7 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29 · Compressive Strength 500 MPa72.5 ksi · Shear Strength 410 MPa59.5 ksi · Hardness, Rockwell C 20 HRC
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,450°C2,642 °F · Liquidus Temperature 1,505°C2,741 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 38 W/m·K22 BTU/hr·ft·°F · Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 12 µm/m·K6.7 µin/in·°F · Latent Heat of Fusion 250 J/g107 BTU/lb · Min Service Temperature -30°C-22 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 5 % IACS · Electrical Resistivity 3.5×10⁻⁷ Ω·m13.8 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.6 V · Corrosion Resistance 25 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 40 / 100 · Polishability 55 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 32 MJ/kg13,758 BTU/lb · Embodied Carbon (primary production) 2.2 kg CO₂/kg · Embodied Water 60 L/kg7.2 gal/lb · Typical Recycled Content 25%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
12CrMoV12-10 +A vs 12CrMoV12-10 +QT+SPWHT — frequently asked
Is 12CrMoV12-10 +QT+SPWHT stronger than 12CrMoV12-10 +A?
Yes. 12CrMoV12-10 +QT+SPWHT has a typical yield strength of 460 MPa (66.7 ksi) against 350 MPa (50.8 ksi) for 12CrMoV12-10 +A — about 31% more. Tensile strength is 630 MPa (91.4 ksi) vs 570 MPa (82.7 ksi).
Which condition does FabDigit quote by default, +A or +QT+SPWHT?
+QT is the default 12CrMoV12-10 condition in the FabDigit quote flow (neither +A nor +QT+SPWHT). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 12CrMoV12-10 +A or 12CrMoV12-10 +QT+SPWHT?
12CrMoV12-10 +A. Its machinability rates good (55/100) against fair (47/100) for 12CrMoV12-10 +QT+SPWHT; for welding the order is 12CrMoV12-10 +A first (fair, 50/100) then 12CrMoV12-10 +QT+SPWHT (fair, 45/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 12CrMoV12-10 +A and 12CrMoV12-10 +QT+SPWHT side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.