Steel 1140-HR vs 1140-IH
Steel · 1140 temper comparison
1140-HR and 1140-IH are two conditions of the same steel grade, 1140: HR (hot rolled) versus IH (induction hardened). The chemistry is identical, so every difference below comes from the condition. 1140-IH is the stronger of the two: yield strength 580 MPa (84.1 ksi) against 345 MPa (50 ksi) for 1140-HR, about 68% more; tensile strength follows at 800 MPa (116 ksi) vs 585 MPa (84.8 ksi). In exchange, 1140-HR is the more ductile: elongation 20% versus 10% for 1140-IH, and 1140-IH is harder (550 HB vs 170 HB). 1140-HR runs hotter in service (400°C vs 180°C continuous) and 1140-HR conducts electricity better (10 % IACS vs 9 % IACS). On the shop floor, 1140-HR machines more easily (good vs poor) and 1140-HR welds better (poor vs not recommended).
1140-HRChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
1140-IHChoose it when strength drives the design.
1140-HR vs 1140-IH: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 205 GPa29.7 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,425°C2,597 °F · Liquidus Temperature 1,495°C2,723 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 486 J/kg·K0.12 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 11.7 µm/m·K6.5 µin/in·°F · Latent Heat of Fusion 247 J/g106 BTU/lb · Min Service Temperature -20°C-4 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.61 V · Corrosion Resistance 10 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 55 / 100 · Polishability 55 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 25 MJ/kg10,748 BTU/lb · Embodied Carbon (primary production) 1.9 kg CO₂/kg · Embodied Water 45 L/kg5.4 gal/lb · Typical Recycled Content 35%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
1140-HR vs 1140-IH — frequently asked
Is 1140-IH stronger than 1140-HR?
Yes. 1140-IH has a typical yield strength of 580 MPa (84.1 ksi) against 345 MPa (50 ksi) for 1140-HR — about 68% more. Tensile strength is 800 MPa (116 ksi) vs 585 MPa (84.8 ksi).
Which condition does FabDigit quote by default, HR or IH?
CD is the default 1140 condition in the FabDigit quote flow (neither HR nor IH). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 1140-HR or 1140-IH?
1140-HR. Its machinability rates good (64/100) against poor (20/100) for 1140-IH; for welding the order is 1140-HR first (poor, 32/100) then 1140-IH (not recommended, 10/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 1140-HR and 1140-IH side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.