Steel 10B38 Annealed vs 10B38-HR
Steel · 10B38 temper comparison
10B38 Annealed and 10B38-HR are two conditions of the same steel grade, 10B38: Annealed versus HR (hot rolled). The chemistry is identical, so every difference below comes from the condition. 10B38-HR is the stronger of the two: yield strength 320 MPa (46.4 ksi) against 285 MPa (41.3 ksi) for 10B38 Annealed, about 12% more; tensile strength follows at 570 MPa (82.7 ksi) vs 515 MPa (74.7 ksi). In exchange, 10B38 Annealed is the more ductile: elongation 25% versus 20% for 10B38-HR, and 10B38-HR is harder (163 HB vs 149 HB).
10B38 AnnealedChoose it when the part is bent, formed or impact-loaded.
10B38-HRChoose it when strength drives the design.
10B38 Annealed vs 10B38-HR: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 205 GPa29.7 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,420°C2,588 °F · Liquidus Temperature 1,500°C2,732 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Same in both: Specific Heat Capacity 470 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 11.7 µm/m·K6.5 µin/in·°F · Latent Heat of Fusion 260 J/g112 BTU/lb · Max Service Temperature (continuous) 400°C752 °F · Min Service Temperature -20°C-4 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 10 % IACS · Electrical Resistivity 1.7×10⁻⁷ Ω·m6.69 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.61 V · Corrosion Resistance 10 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 65 / 100 · Polishability 55 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 25 MJ/kg10,748 BTU/lb · Embodied Carbon (primary production) 2 kg CO₂/kg · Embodied Water 45 L/kg5.4 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
10B38 Annealed vs 10B38-HR — frequently asked
Is 10B38-HR stronger than 10B38 Annealed?
Yes. 10B38-HR has a typical yield strength of 320 MPa (46.4 ksi) against 285 MPa (41.3 ksi) for 10B38 Annealed — about 12% more. Tensile strength is 570 MPa (82.7 ksi) vs 515 MPa (74.7 ksi).
Which condition does FabDigit quote by default, Annealed or HR?
HR is the default 10B38 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which welds better, 10B38 Annealed or 10B38-HR?
10B38 Annealed. Its weldability rates good (60/100) against good (55/100) for 10B38-HR.