Steel 1030 Annealed vs 1030-CR
Steel · 1030 temper comparison
1030 Annealed and 1030-CR are two conditions of the same steel grade, 1030: Annealed versus CR (cold rolled). The chemistry is identical, so every difference below comes from the condition. 1030-CR is the stronger of the two: yield strength 460 MPa (66.7 ksi) against 341 MPa (49.5 ksi) for 1030 Annealed, about 35% more; tensile strength follows at 550 MPa (79.8 ksi) vs 463 MPa (67.2 ksi). In exchange, 1030 Annealed is the more ductile: elongation 31% versus 12% for 1030-CR, and 1030-CR is harder (160 HB vs 126 HB). 1030 Annealed runs hotter in service (400°C vs 300°C continuous).
1030 AnnealedChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
1030-CRChoose it when strength drives the design.
1030 Annealed vs 1030-CR: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Same in both: Elastic (Young's) Modulus 205 GPa29.7 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,425°C2,597 °F · Liquidus Temperature 1,510°C2,750 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 51.9 W/m·K30 BTU/hr·ft·°F · Specific Heat Capacity 486 J/kg·K0.12 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 11.7 µm/m·K6.5 µin/in·°F · Latent Heat of Fusion 247 J/g106 BTU/lb · Min Service Temperature -20°C-4 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 10 % IACS · Electrical Resistivity 1.7×10⁻⁷ Ω·m6.69 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.61 V · Corrosion Resistance 10 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 45 / 100 · Brazeability / Solderability 70 / 100 · Polishability 55 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 25 MJ/kg10,748 BTU/lb · Embodied Carbon (primary production) 1.9 kg CO₂/kg · Embodied Water 40 L/kg4.8 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
1030 Annealed vs 1030-CR — frequently asked
Is 1030-CR stronger than 1030 Annealed?
Yes. 1030-CR has a typical yield strength of 460 MPa (66.7 ksi) against 341 MPa (49.5 ksi) for 1030 Annealed — about 35% more. Tensile strength is 550 MPa (79.8 ksi) vs 463 MPa (67.2 ksi).
Which condition does FabDigit quote by default, Annealed or CR?
HR is the default 1030 condition in the FabDigit quote flow (neither Annealed nor CR). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 1030 Annealed or 1030-CR?
1030-CR, by a small margin. Both rate good for machinability — 62/100 against 55/100 for 1030 Annealed; for welding the order is 1030 Annealed first (good, 65/100) then 1030-CR (good, 60/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 1030 Annealed and 1030-CR side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.