Steel 1026-CR vs 1026-HR
Steel · 1026 temper comparison
1026-CR and 1026-HR are two conditions of the same steel grade, 1026: CR (cold rolled) versus HR (hot rolled). The chemistry is identical, so every difference below comes from the condition. 1026-CR is the stronger of the two: yield strength 370 MPa (53.7 ksi) against 275 MPa (39.9 ksi) for 1026-HR, about 35% more; tensile strength follows at 470 MPa (68.2 ksi) vs 440 MPa (63.8 ksi). In exchange, 1026-HR is the more ductile: elongation 24% versus 18% for 1026-CR, and 1026-CR is harder (140 HB vs 126 HB). 1026-HR runs hotter in service (400°C vs 300°C continuous).
1026-CRChoose it when strength drives the design.
1026-HRChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
1026-CR vs 1026-HR: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Same in both: Elastic (Young's) Modulus 200 GPa29 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 140 GPa20.3 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,425°C2,597 °F · Liquidus Temperature 1,515°C2,759 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 51.9 W/m·K30 BTU/hr·ft·°F · Specific Heat Capacity 486 J/kg·K0.12 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 11.9 µm/m·K6.6 µin/in·°F · Latent Heat of Fusion 250 J/g107 BTU/lb · Min Service Temperature -30°C-22 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 10.8 % IACS · Electrical Resistivity 1.6×10⁻⁷ Ω·m6.3 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.61 V · Corrosion Resistance 10 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Polishability
Same in both: Weldability 85 / 100 · Brazeability / Solderability 75 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 25 MJ/kg10,748 BTU/lb · Embodied Carbon (primary production) 1.9 kg CO₂/kg · Embodied Water 40 L/kg4.8 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
1026-CR vs 1026-HR — frequently asked
Is 1026-CR stronger than 1026-HR?
Yes. 1026-CR has a typical yield strength of 370 MPa (53.7 ksi) against 275 MPa (39.9 ksi) for 1026-HR — about 35% more. Tensile strength is 470 MPa (68.2 ksi) vs 440 MPa (63.8 ksi).
Which condition does FabDigit quote by default, CR or HR?
HR is the default 1026 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose 1026-CR over 1026-HR?
Pick 1026-CR when strength drives the design. Pick 1026-HR when the part is bent, formed or impact-loaded, or when the part sees heat.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 1026-CR and 1026-HR side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.