Steel 1018-HR vs 1018 Normalized
Steel · 1018 temper comparison
1018-HR and 1018 Normalized are two conditions of the same steel grade, 1018: HR (hot rolled) versus Normalized. The chemistry is identical, so every difference below comes from the condition. 1018 Normalized is the stronger of the two: yield strength 340 MPa (49.3 ksi) against 220 MPa (31.9 ksi) for 1018-HR, about 55% more; tensile strength follows at 440 MPa (63.8 ksi) vs 400 MPa (58 ksi). 1018 Normalized is the more ductile: elongation 32% versus 25% for 1018-HR, and 1018 Normalized is harder (126 HB vs 116 HB).
1018 NormalizedChoose it when strength drives the design, or when the part is bent, formed or impact-loaded.
1018-HR vs 1018 Normalized: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Same in both: Elastic (Young's) Modulus 205 GPa29.7 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 140 GPa20.3 Msi · Poisson's Ratio 0.29 · Compressive Strength 220 MPa31.9 ksi · Shear Strength 250 MPa36.3 ksi · Fracture Toughness (K_IC) 110 MPa·√m100 ksi·√in · Hardness, Vickers 122 HV
Physical
Density and transition temperatures.
Same in both: Density 7.87 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,425°C2,597 °F · Liquidus Temperature 1,510°C2,750 °F
Thermal
How each material carries heat and how hot it can run.
Min Service Temperature
Same in both: Thermal Conductivity 51.9 W/m·K30 BTU/hr·ft·°F · Specific Heat Capacity 486 J/kg·K0.12 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 11.7 µm/m·K6.5 µin/in·°F · Latent Heat of Fusion 247 J/g106 BTU/lb · Max Service Temperature (continuous) 400°C752 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 10.8 % IACS · Electrical Resistivity 1.6×10⁻⁷ Ω·m6.3 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.61 V · Corrosion Resistance 10 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability Rating (AISI 1212 = 100 %)
Same in both: Machinability 58 / 100 · Weldability 95 / 100 · Formability (cold) 85 / 100 · Brazeability / Solderability 75 / 100 · Polishability 50 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 25 MJ/kg10,748 BTU/lb · Embodied Carbon (primary production) 1.9 kg CO₂/kg · Embodied Water 45 L/kg5.4 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
1018-HR vs 1018 Normalized — frequently asked
Is 1018 Normalized stronger than 1018-HR?
Yes. 1018 Normalized has a typical yield strength of 340 MPa (49.3 ksi) against 220 MPa (31.9 ksi) for 1018-HR — about 55% more. Tensile strength is 440 MPa (63.8 ksi) vs 400 MPa (58 ksi).
Which condition does FabDigit quote by default, HR or Normalized?
HR is the default 1018 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose 1018-HR over 1018 Normalized?
Pick 1018 Normalized when strength drives the design, or when the part is bent, formed or impact-loaded.