Steel 100CrMn6 +A vs 100CrMn6 +C
Steel · 100CrMn6 temper comparison
100CrMn6 +A and 100CrMn6 +C are two conditions of the same steel grade, 100CrMn6: +A (annealed) versus +C (cold drawn). The chemistry is identical, so every difference below comes from the condition. 100CrMn6 +C is the stronger of the two: yield strength 620 MPa (89.9 ksi) against 410 MPa (59.5 ksi) for 100CrMn6 +A, about 51% more; tensile strength follows at 780 MPa (113 ksi) vs 660 MPa (95.7 ksi). In exchange, 100CrMn6 +A is the more ductile: elongation 22% versus 10% for 100CrMn6 +C, and 100CrMn6 +C is harder (235 HB vs 200 HB).
100CrMn6 +AChoose it when the part is bent, formed or impact-loaded.
100CrMn6 +CChoose it when strength drives the design.
100CrMn6 +A vs 100CrMn6 +C: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 210 GPa30.5 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.3
Physical
Density and transition temperatures.
Same in both: Density 7.81 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,400°C2,552 °F · Liquidus Temperature 1,450°C2,642 °F
Thermal
How each material carries heat and how hot it can run.
Same in both: Thermal Conductivity 44 W/m·K25.4 BTU/hr·ft·°F · Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 11.7 µm/m·K6.5 µin/in·°F · Latent Heat of Fusion 250 J/g107 BTU/lb · Max Service Temperature (continuous) 150°C302 °F · Min Service Temperature -40°C-40 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 6 % IACS · Electrical Resistivity 3×10⁻⁷ Ω·m11.8 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.65 V · Corrosion Resistance 12 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Same in both: Weldability 12 / 100 · Brazeability / Solderability 40 / 100 · Polishability 85 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 32 MJ/kg13,758 BTU/lb · Embodied Carbon (primary production) 2.3 kg CO₂/kg · Embodied Water 60 L/kg7.2 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
100CrMn6 +A vs 100CrMn6 +C — frequently asked
Is 100CrMn6 +C stronger than 100CrMn6 +A?
Yes. 100CrMn6 +C has a typical yield strength of 620 MPa (89.9 ksi) against 410 MPa (59.5 ksi) for 100CrMn6 +A — about 51% more. Tensile strength is 780 MPa (113 ksi) vs 660 MPa (95.7 ksi).
Which condition does FabDigit quote by default, +A or +C?
+A is the default 100CrMn6 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose 100CrMn6 +A over 100CrMn6 +C?
Pick 100CrMn6 +A when the part is bent, formed or impact-loaded. Pick 100CrMn6 +C when strength drives the design.