Steel 1.2842 Annealed vs 1.2842-QT200
Steel · 1.2842 temper comparison
1.2842 Annealed and 1.2842-QT200 are two conditions of the same steel grade, 1.2842: Annealed versus QT200 (Q&T 200 °C). The chemistry is identical, so every difference below comes from the condition. 1.2842-QT200 is the stronger of the two: yield strength 2,000 MPa (290 ksi) against 420 MPa (60.9 ksi) for 1.2842 Annealed, about 4.8 times as much; tensile strength follows at 2,250 MPa (326 ksi) vs 700 MPa (102 ksi). In exchange, 1.2842 Annealed is the more ductile: elongation 16% versus 1% for 1.2842-QT200, and 1.2842-QT200 is harder (61 HRC vs 17 HRC). 1.2842 Annealed runs hotter in service (400°C vs 170°C continuous) and 1.2842 Annealed conducts electricity better (7 % IACS vs 6 % IACS). On the shop floor, 1.2842 Annealed machines more easily (fair vs not recommended) and 1.2842 Annealed welds better (poor vs not recommended).
1.2842 AnnealedChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
1.2842-QT200Choose it when strength drives the design.
1.2842 Annealed vs 1.2842-QT200: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Rockwell C
Hardness, Vickers
Same in both: Shear Modulus 81 GPa11.7 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29 · Hardness, Brinell 215 HB · Hardness, Rockwell B 95 HRB
Physical
Density and transition temperatures.
Same in both: Density 7.8 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,420°C2,588 °F · Liquidus Temperature 1,470°C2,678 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 12.5 µm/m·K6.9 µin/in·°F · Latent Heat of Fusion 250 J/g107 BTU/lb · Min Service Temperature -30°C-22 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.6 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 20 / 100 · Brazeability / Solderability 40 / 100 · Polishability 65 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 34 MJ/kg14,617 BTU/lb · Embodied Carbon (primary production) 2.4 kg CO₂/kg · Embodied Water 65 L/kg7.8 gal/lb · Typical Recycled Content 35%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
1.2842 Annealed vs 1.2842-QT200 — frequently asked
Is 1.2842-QT200 stronger than 1.2842 Annealed?
Yes. 1.2842-QT200 has a typical yield strength of 2,000 MPa (290 ksi) against 420 MPa (60.9 ksi) for 1.2842 Annealed — about 4.8 times as much. Tensile strength is 2,250 MPa (326 ksi) vs 700 MPa (102 ksi).
Which condition does FabDigit quote by default, Annealed or QT200?
Annealed is the default 1.2842 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 1.2842 Annealed or 1.2842-QT200?
1.2842 Annealed. Its machinability rates fair (45/100) against not recommended (8/100) for 1.2842-QT200; for welding the order is 1.2842 Annealed first (poor, 20/100) then 1.2842-QT200 (not recommended, 5/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 1.2842 Annealed and 1.2842-QT200 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.