Steel 1.2601 Annealed vs 1.2601 Q&T 62-64 HRC
Steel · 1.2601 temper comparison
1.2601 Annealed and 1.2601 Q&T 62-64 HRC are two conditions of the same steel grade, 1.2601: Annealed versus Q&T 62-64 HRC (hardened ~980 °C, tempered ~150–180 °C). The chemistry is identical, so every difference below comes from the condition. 1.2601 Q&T 62-64 HRC is the stronger of the two: yield strength 2,100 MPa (305 ksi) against 500 MPa (72.5 ksi) for 1.2601 Annealed, about 4.2 times as much; tensile strength follows at 2,350 MPa (341 ksi) vs 800 MPa (116 ksi). In exchange, 1.2601 Annealed is the more ductile: elongation 12% versus 0.5% for 1.2601 Q&T 62-64 HRC, and 1.2601 Q&T 62-64 HRC is harder (63 HRC vs 20 HRC). 1.2601 Annealed runs hotter in service (200°C vs 160°C continuous). On the shop floor, 1.2601 Annealed machines more easily (poor vs not recommended).
1.2601 AnnealedChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
1.2601 Q&T 62-64 HRCChoose it when strength drives the design.
1.2601 Annealed vs 1.2601 Q&T 62-64 HRC: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
1.2601 Annealed1.2601 Q&T 62-64 HRC
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Rockwell C
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 210 GPa30.5 Msi · Shear Modulus 81 GPa11.7 Msi · Bulk Modulus 165 GPa23.9 Msi · Poisson's Ratio 0.29 · Reduction in Area 20% · Hardness, Brinell 230 HB · Hardness, Rockwell B 98 HRB
Physical
Density and transition temperatures.
Same in both: Density 7.7 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,260°C2,300 °F · Liquidus Temperature 1,400°C2,552 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 20 W/m·K11.6 BTU/hr·ft·°F · Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 10.8 µm/m·K6 µin/in·°F · Latent Heat of Fusion 250 J/g107 BTU/lb · Min Service Temperature -40°C-40 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Polishability 75 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 34 MJ/kg14,617 BTU/lb · Embodied Carbon (primary production) 2.5 kg CO₂/kg · Embodied Water 65 L/kg7.8 gal/lb · Typical Recycled Content 40%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
1.2601 Annealed vs 1.2601 Q&T 62-64 HRC — frequently asked
Is 1.2601 Q&T 62-64 HRC stronger than 1.2601 Annealed?
Yes. 1.2601 Q&T 62-64 HRC has a typical yield strength of 2,100 MPa (305 ksi) against 500 MPa (72.5 ksi) for 1.2601 Annealed — about 4.2 times as much. Tensile strength is 2,350 MPa (341 ksi) vs 800 MPa (116 ksi).
Which condition does FabDigit quote by default, Annealed or Q&T 62-64 HRC?
Annealed is the default 1.2601 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 1.2601 Annealed or 1.2601 Q&T 62-64 HRC?
1.2601 Annealed. Its machinability rates poor (32/100) against not recommended (4/100) for 1.2601 Q&T 62-64 HRC; for welding the order is 1.2601 Annealed first (not recommended, 12/100) then 1.2601 Q&T 62-64 HRC (not recommended, 5/100).