Stainless Steel Zeron 100 Cold Drawn vs Zeron 100 Solution Annealed
Stainless Steel · Zeron 100 temper comparison
Zeron 100 Cold Drawn and Zeron 100 Solution Annealed are two conditions of the same stainless steel grade, Zeron 100: Cold Drawn versus Solution Annealed. The chemistry is identical, so every difference below comes from the condition. Zeron 100 Cold Drawn is the stronger of the two: yield strength 790 MPa (115 ksi) against 620 MPa (89.9 ksi) for Zeron 100 Solution Annealed, about 27% more; tensile strength follows at 950 MPa (138 ksi) vs 830 MPa (120 ksi). In exchange, Zeron 100 Solution Annealed is the more ductile: elongation 30% versus 20% for Zeron 100 Cold Drawn, and Zeron 100 Cold Drawn is harder (300 HB vs 250 HB).
Zeron 100 Cold DrawnChoose it when strength drives the design.
Zeron 100 Solution AnnealedChoose it when the part is bent, formed or impact-loaded.
Zeron 100 Cold Drawn vs Zeron 100 Solution Annealed: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Zeron 100 Cold DrawnZeron 100 Solution Annealed
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell C
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 200 GPa29 Msi · Shear Modulus 77 GPa11.2 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.3
Physical
Density and transition temperatures.
Same in both: Density 7.8 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,350°C2,462 °F · Liquidus Temperature 1,400°C2,552 °F
Thermal
How each material carries heat and how hot it can run.
Same in both: Thermal Conductivity 14.7 W/m·K8.5 BTU/hr·ft·°F · Specific Heat Capacity 482 J/kg·K0.12 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 12.8 µm/m·K7.1 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Max Service Temperature (continuous) 280°C536 °F · Min Service Temperature -50°C-58 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 2 % IACS · Electrical Resistivity 8.5×10⁻⁷ Ω·m33.5 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.15 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 55 / 100 · Brazeability / Solderability 35 / 100 · Polishability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 58 MJ/kg24,936 BTU/lb · Embodied Carbon (primary production) 4.5 kg CO₂/kg · Embodied Water 130 L/kg15.6 gal/lb · Typical Recycled Content 55%
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Zeron 100 Cold Drawn vs Zeron 100 Solution Annealed — frequently asked
Is Zeron 100 Cold Drawn stronger than Zeron 100 Solution Annealed?
Yes. Zeron 100 Cold Drawn has a typical yield strength of 790 MPa (115 ksi) against 620 MPa (89.9 ksi) for Zeron 100 Solution Annealed — about 27% more. Tensile strength is 950 MPa (138 ksi) vs 830 MPa (120 ksi).
Which condition does FabDigit quote by default, Cold Drawn or Solution Annealed?
Solution Annealed is the default Zeron 100 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which welds better, Zeron 100 Cold Drawn or Zeron 100 Solution Annealed?
Zeron 100 Solution Annealed. Its weldability rates good (65/100) against good (60/100) for Zeron 100 Cold Drawn.
Ready to make it?
Upload a CAD file and FabDigit prices the part in Zeron 100 Cold Drawn and Zeron 100 Solution Annealed side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.