Stainless Steel SUS317J2 1/2H vs SUS317J2 1/4H
Stainless Steel · SUS317J2 temper comparison
SUS317J2 1/2H and SUS317J2 1/4H are two conditions of the same stainless steel grade, SUS317J2: 1/2H (half hard) versus 1/4H (quarter hard). The chemistry is identical, so every difference below comes from the condition. SUS317J2 1/2H is the stronger of the two: yield strength 760 MPa (110 ksi) against 600 MPa (87 ksi) for SUS317J2 1/4H, about 27% more; tensile strength follows at 1,000 MPa (145 ksi) vs 860 MPa (125 ksi). In exchange, SUS317J2 1/4H is the more ductile: elongation 25% versus 15% for SUS317J2 1/2H, and SUS317J2 1/2H is harder (300 HB vs 250 HB). SUS317J2 1/4H runs hotter in service (350°C vs 300°C continuous).
SUS317J2 1/2HChoose it when strength drives the design.
SUS317J2 1/4HChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
SUS317J2 1/2H vs SUS317J2 1/4H: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 195 GPa28.3 Msi · Shear Modulus 76 GPa11 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Same in both: Density 8 g/cm³0.29 lb/in³ · Melting Point (Solidus) 1,370°C2,498 °F · Liquidus Temperature 1,400°C2,552 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 13 W/m·K7.5 BTU/hr·ft·°F · Specific Heat Capacity 500 J/kg·K0.12 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 16 µm/m·K8.9 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 2 % IACS · Electrical Resistivity 8.5×10⁻⁷ Ω·m33.5 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.05 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 60 / 100 · Polishability 80 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 60 MJ/kg25,795 BTU/lb · Embodied Carbon (primary production) 4.5 kg CO₂/kg · Embodied Water 130 L/kg15.6 gal/lb · Typical Recycled Content 55%
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
SUS317J2 1/2H vs SUS317J2 1/4H — frequently asked
Is SUS317J2 1/2H stronger than SUS317J2 1/4H?
Yes. SUS317J2 1/2H has a typical yield strength of 760 MPa (110 ksi) against 600 MPa (87 ksi) for SUS317J2 1/4H — about 27% more. Tensile strength is 1,000 MPa (145 ksi) vs 860 MPa (125 ksi).
Which condition does FabDigit quote by default, 1/2H or 1/4H?
Annealed is the default SUS317J2 condition in the FabDigit quote flow (neither 1/2H nor 1/4H). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which welds better, SUS317J2 1/2H or SUS317J2 1/4H?
SUS317J2 1/4H. Its weldability rates good (65/100) against good (60/100) for SUS317J2 1/2H.
Ready to make it?
Upload a CAD file and FabDigit prices the part in SUS317J2 1/2H and SUS317J2 1/4H side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.